模具技术2012.No.6
文章编号：1001-4934(2012)06-0001-04
拉深筋对板料拉深成形的影响
周起涛，鹿晓阳，许毅敏，刘楹樾
（山东建筑大学材料学院，山东济南250101）
摘要：分析了拉深筋对板料拉深成形的影响机理和作用，提出拉深筋的基本设置原
1
则，阐述设计其几何参数时应考感的固素。结合汽车挡泥板的成形过程，利用有限元软件Dynaform分别模拟了无拉深筋、有整体拉深筋和局部拉深筋时挡泥板的成形过程。模拟结果证明，合理的拉深筋参数和布局能够有效地解决成形件的起皱和破裂问题，提高板料拉深成形质量。
关键词：板料成形；拉深筋；数值模拟；局部
中图分类号：TG386
文献标识码：A
Influence of draw bead on sheet metal drawing ZHOU Qi-tao,LUXiao-yang,XUYi-min,LIUYing-yue
Abstract: The influence mechanism and the effect of draw bead on sheet metal drawing was analyzed and the basic principle of setting draw bead was putting forward. At last, the fac-tors to be taken into account in designing the geometric parameters was elaborated. Com bined with the automobile fender forming process, using finite element analysis software Dynaform to simulate the fender forming process with non-draw bead, whole circle draw bead and local draw bead. The result shows that reasonable draw bead parameters and lay out can effectively solve the problem of wrinkling and rupture, in this way improving the quality of sheet metal drawing.
Keywords: sheet metal forming; draw bead; numerical simulation; local
引言 0
板料拉深成形作为一种重要的塑性成形方法，在汽车、航空、航天等领域广泛应用。在板料拉深过程中由于材料流动不一致，尤其是形状复杂以及难成形零件的拉深成形中，很容易出现起皱、破裂、未充分成形等缺陷。为了防止这些缺陷的产生，常采取在模具上设置拉深筋
收稿日期：2012-09-07
作者简介：周起涛（1984一），男，硕士研究生。
的措施，通过调节和控制材料的流动来提高拉深件成形质量"。已有学者在拉深筋阻力、夹持力等关键力能参数的形成机理、构成及其影响因素等方面的研究取得了显著成果，并将研究方向转向对拉深筋的现代设计方法[2-33。无论对拉深筋的设计如何，其最终目的是为了获得合适的拉深筋阻力来控制板料成形时的边界条件[4]。