ISSN1000 3762 HL/8 1
轴承2016年8期 Bearing 2016 , No. 8
钢制保持架冲压模具性能分析
蔚建，杨建文，张德龙，王志伟
（洛阳LYC轴承有限公司，河南洛阳471039）
24 26
摘要：分析影响钢制保持架冲压凹模寿命的各种因素，分别选用GCr15SiMn，GCr15和SLM-11这3种模具材料进行工艺试验，对多个型号、不同材料的保持架进行冲压加工，通过对凹模性能、经济效率等方面的对比，指出了SLM-11材料凹模的优越性
关键词：钢制保持架；冲压模具：回模寿命：模具材料：工艺试验
中图分类号：TH133.33;TG386.49
文献标志码：B
文章编号：10003762(2016)08002403
Analysis onPerformancesofStampedDieforCagesMadeofSteel
Wei Jian,Yang Jianwen,Zhang Delong,Wang Zhiwei( Luoyang LYC Bearing Co. , Lid. ,Luoyang 471039, China)
Abstract: The different factors influencing life of stamped concave die are analyzed for cages made of steel, the GCrl5SiMn, GCr15 and SLM 11 are respectively chosen for process test., The stamping processing of many diferent types of cages made of diferent materials is carried out. The superiority of concave die made of material SLM 1lis ob-
tained through comparison and consideration of performances of concave die and economic efficiency. Key words : cage made of steel; stamped die; life of concave die; material of die; process test
钢保持架冲窗孔工序，使用高耐磨性、高冲击
韧性模具材料，可以极大地延长模具寿命，降低损耗，大幅提升生产效率，为企业节约成本。因此，对保持架冲压模具进行性能试验，选择更加合理
的模具材料十分必要。 1
凹模寿命影响因素 1.1概念
1)凹模寿命：以单个凹模冲出合格制品的件数来衡量。
2)凹模失效：凹模的主要失效形式为刃口磨损、压塌、崩刃、胀裂等，其中刃口磨损属于正常失效。刃口磨钝后会使冲裁件的毛刺增大，尺寸精度和断面质量下降，当刃口磨损到一定程度后，凹
收稿日期：2016-01-18；修回日期：2016-03-23 基金项目：企业内部基金项目（KY-2016-31）
作者简介：蔚建（1987一），男，设计员，助理工程师，主要从事模具设计和工艺编制工作，E-mail：weijian303@126. com。
模就不能正常工作，这时必须刃磨或更换模具零件，甚至模具报废。试验使用的冲裁凹模如图1 所示。
图1凹模
Fig. 1 Concave die
1.2
主要影响因素
凹模寿命与凸、凹模具材料、模具热处理质
量、工件加工精度、冲裁间隙、冲裁件材质、机床和模具的调整情况等有关。下面着重分析几点主要因素。
1)凹模材料。目前广泛使用且具有代表性的冲孔模具材料主要有GCrl5SiMn，GCr15。试验将根据生产加工中存在的一系列情况，首次选择高耐磨性、高冲击韧性模具材料SLM-11，
2)冲裁间隙。冲裁间隙对冲裁件质量、模具寿命等影响很大。当模具间隙减小时，接触面上