ISSN1000 3762 CN41 1148/TH
轴承2017年1期 Bearing 2017 , No. 1
35 36,53
D0I: 10. 19533/j. issn1000 3762. 2017. 01. 010
钢制实体保持架镀银表面缺陷分析
李迎丽，赵燕，杜长权
（中航工业哈尔滨轴承有限公司，哈尔滨150036）
摘要：针对40CrNiMoA钢制实体保持架镀银后在其表面出现针刺状麻点缺陷问题，分析影响保持架镀银质量的多种原因，通过多项工艺试验表明：保持架表面贴附细小金属切屑，清洗过程很难去除，通过优化保持架光饰工
艺，解决了钢制保持架镀银麻点缺陷，保证了镀银质量，满足了产品要求。关键词：滚动轴承：实体保持架；40CrNiMoA；镀银；缺陷分析：光饰：工艺试验
中图分类号：TH133.33；TG153.1*6
文献标志码：B
文章编号：10003762(2017)01003502
Surface Defect Analysis of SteelSold Cage Sliver Plated
Li Yingli,ZhaoYan,Du Changquan
( AVIC Harbin Bearing Co. ,Lid. ,Harbin 150036, China)
Abstract : For 40CrNiMoA steel solid cage, acupuncture like pitting defects appear on the surface after silver plating and the a variety of reasons impacting silver plating quality are analyzed. Prooess test show that small metal chips atta ched to the surface are root cause of pitting, which are difficult to remove in cleaning process, and the steel cage silver pitting defects are avoided by optimizing the cage finishing prooess, ensuring the quality of silver plating to meet the product requirements.
Key words: rolling bearing; solid cage:40CrNiMoA ;sliver plating; defect analysis; finishing; process test
1
问题的提出
40CrNiMoA是一种合金结构钢，具有优良的抗疲劳和耐磨性能[1]，因此多种轴承实体保持架选用该材料，以提升轴承使用性能。保持架完成机加工后采用镀银方法进行表面化学处理，提高轴承自润滑能力，进一步延长轴承使用寿命2。保持架镀银质量的主要检测指标包括表面质量、镀银层结合力、镀银层厚度等，其中表面质量是一项非常直观且重要的指标。
40CrNiMoA保持架机加工及镀银质量一直保
持稳定，但近阶段保持架镀银后，外径、内径表面出现针刺状密密麻麻的麻点缺陷（图1），而脱银处理后按照现行镀银工艺重新镀银后，缺陷消失，镀银质量又达到了标准要求。但重复加工既造成
收稿日期：2016-05-13；修回日期：2016-07-29
作者简介：李迎丽(1971一），女，汉族，高级工程师，主要从事轴承实体保持架加工工艺、工装设计及技术指导等工
作,E mail ;liy19@ 163. com 万方数据
经济损失，又影响生产进度，其至影响用户装机使用。因此对缺陷原因进行分析，并通过工艺试验予以验证。
图1针刺状廉点缺陷
Fig. 1 Acupuncture like pitting defects 镀银缺陷原因分析
根据保持架镀银缺陷情况，初步判定缺陷与
镀银前的保持架表面清洁状态有关。梳理 40CrNiMoA保持架加工工艺流程，分析镀银前保