第42卷第3期
2014年3月【助剂】
聚氯乙烯 Polyvinyl Chloride
Vol.42,No.3 Mar.，2014
助剂对PVC/MBS体系塑化性能和流变性能的影响
华海英·
（沈阳市于洪区公路管理处，辽宁沈阳110141）
【关键调］PVC;MBS；助剂；流变性能；塑化性能
[摘要】测试了助剂对PVC/MBS体系塑化性能及流变性能的影响。结果表明：①改性树脂AS的加人，能够明显改变PVC/MBS体系的塑化行为，缩短望化时间，类似于PVC内润滑剂的流变效果，当AS用量提高到4份时，PVC/MBS体系表现出塑化过快、塑化扭矩过高的特征；②随着润滑剂用量的增加，PVC/MBS体系的塑化扭矩降低，塑化时间延长；试验温度升高，PVC/MBS体系的黏度减小，平衡扭矩降低。
【中图分类号】TQ325.5
【文献标志码】B
【文章编号】10097937(2014)03002303
Effects of additives on the rheological property and plasticizingproperty
ofPVC/MBScomposites
BI Haiying
(Shenyang Yuhong District Highway Management Office, Shenyang 110041, China) Key words: PVC; MBS; aid; rheological property; plasticizing property
Abstract: Effects of additives on the rheological property and plasticizing property of PVC/MBS composites were tested. The results showed that: ① AS modified resin could obviously improve the plas-ticizing behavior of MBS/PVC composites, shorten the plastcizing times, its rheological effect was similar to that of inner lubricant for PVC. When the dosages of AS were 4 parts, the PVC/MBS composite had the characteristics of excessive plasticizing speed and overhigh plasticizing torque. ② With the increase of lubricant dosages, the plasticizing torque of PVC/MBS composite was reduced and the plasticizing time was prolonged; with the increase of test temperature, the viscosity of PVC/MBS composite was decreased and the balance torque was reduced.
MBS作为硬质PVC的冲击改性剂，不仅可提高PVC的冲击性能，也对共混体系的加工性能（如分散、熔融、熔体流变性能等)产生很大影响。MBS 的加人大大提高了共混体系的黏度，使其加工变得困难。改性树脂、润滑剂等助剂的加入能够改善 PVC材料的加工性能，笔者考察了助剂和试验温度对PVC/MBS体系塑化性能、流变性能的影响。
1试验 1.1原材料
PVC，中国石油化工股份有限公司齐鲁分公司氯碱厂；MBS，日本进口；改性树脂AS，台湾奇美公
，【收稿日期】2014-01=11
司；有机锡稳定剂、润滑剂，市售；活性超细碳酸钙，
常州碳酸钙有限公司。 1.2仪器
高速搅拌机，张家港万塑机械有限公司：AC ER2000毛细管挤出流变仪，美国TA公司；哈克转
矩流变仪，德国HAAKE公司。 1.3试验方法
(1)塑化性能：采用哈克转矩流变仪测试，试验温度为170、180、190℃，转子转速为40/min，加料量为58g，塑化时间为7min。
(2)流变性能：采用毛细管流变仪测试，毛细管
【作者简介】毕海英（1976一），女，工程师，1998年毕业于辽宁石油化工大学高分子化工专业，现任沈阳市于洪区公路
管理处试验检测中心主任，主要从事公路材料的生产管理、检测、研发等工作。
23
万方数据