分散剂对PVC树脂性能的影响
刘容德，，李静，刘浩，张桦
（中国石油化工股份有限公司齐鲁分公司研究院，山东博255400）
【关键调］PVC；分收剂：分散性能；加工应用
Vol.44,No.5 May，2016
[摘要】研究了采用进口分做剂替代国产分散剂制备的PVC树脂的性能。结果表明：替代后PVC树脂的老化白度提高，颗粒形态变得更为规整，树脂颗粒内部孔隙数量明显增多，增塑剂吸收时间缩短。加工应用试验表明：更换分散剂后，生产的制品具有较高的透光率、较低的黄色指数和雾度。
中图分类号】TQ325.3
文献标志码］B
[文章编号】10097937(2016)05002207
Effects of dispersing agents on properties of PVC resins
LIU Rongde,LI Jing,LIU Hao,ZHANG Hua
(ResearchInstituteof QiluBranch Co.,SINOPEC，Zibo255400,China)
Key words: PVC; dispersant; dispersion property; processing and application
Abstract: The properties of PVC resins prepared at presence of imported dispersants instead of do mestic dispersants were studied. The results showed that the aging whiteness of the PVC resins improved, the particle morphology became more regular, the number of internal pores of resin particles increased ob-viously, and the plasticizer absorption time was shortened. The test results of processing and application showed that the products produced from the PVC resins had higher transmittance, lower yellow index and haze.
近年来，由于电石法PVC企业不断新增产能，乙烯法PVC企业受到了巨大的冲击，生产经营面临较大的压力，处于亏损状态。据中国氯碱工业协会统计,2014年我国PVC产能达到2654万a，开工率为61.4%，表观消费量为1587万t，我国PVC行业面临严峻的产能过剩局面。与电石法PVC相比，乙烯法PVC具有安全、环保、节能、质优等特点，而且在高档透明制品领域有着电石法PVC树脂无法替代的优势，因而乙烯法仍将是我国必不可少的种PVC生产工艺，也是最可与国外乙烯法PVC抗衡的工艺路线。
各PVC企业为解决目前困境，纷纷开发新的树脂牌号，开发高附加值的特种树脂产品，提高树脂性能，从聚合源头上提高树脂内在质量等。聚合用助剂、聚合工艺参数等都将影响到PVC树脂的性能。笔者就更换聚合分散剂后PVC树脂的基本性能及
【收稿日期】201602-03
加工应用进行了研究，以找出进口分散剂替代国产分散剂后树脂的性能特点，为树脂的加工及应用提
供数据参考。 1试验部分 1.1原材料
PVC,S-800、S-1000，中国石油化工股份有限公司齐鲁分公司氯碱厂；PVC，S-60，台塑公司； PVC-SG7.国产：有机锡稳定剂TM-181.美国：海滑剂ZB-60、ZB-74，淄博华星助剂有限公司：硬脂酸钙，淄博塑料助剂厂；ACR-401，淄博华星助
剂有限公司；硬脂酸，国产。 1.2仪器及设备
光电雾度仪WGW，上海第三光学仪器厂；表观密度测定仪BMY-I，金建检测仪器有限公司；白度计WSB-Ⅱ，温州仪器仪表有限公司：显微镜
【作者简介】刘容德（1968—），男，高级工程师，1989年毕业于青岛科技大学高分子材料系，现从事PVC树脂改性方
面的研究。 22
万方数据