第39卷第3期
2011年3月【材料与性能】
聚氰乙烯 Polyvinyl Chloride
末粉特性对PVC/市塑发泡材料性能的影响
贾小波，李静，对浩
（中国石油化工股份有限公司齐鲁分公司研究院，山东漏博255400）
［关键词］木粉；PVC;发泡性能
Vol.39,No.3 Mar.，2011
[摘要］对木粉进行了热重分析，考察了木粉粒径及表面处理方法对PVC/木塑发泡材料性能的影响。结果表明：果用粒径117μm(120月）、经过硅烷类偶联剂处理的木粉制得的PVC/本塑发泡材料的综合性能较优；相同发泡剂用量下，PVC/木塑发泡材料密度随粉用量的增加而增大，发泡效果变差。
［中图分类号］TQ325.3
[文献标志码］B
［文章编号］】10097937(2011)03-0024-04
Influences of wood powder characteristics on properties of PVC/wood powder foaming materials
JIAXiaobo,LIJing,LIUHao
(Rcsearch Institute of QiluBranchCo.,SINOPEC,Zibo255400,China)
Key words; wood powder; PVC; foaming propcrty
Abstract: Wood powder was analyzed by thermogravimetry, and influcnces of particle size and surface treatment mcthods of wood powder on propcrties of PVC/wood powder foaming materials were investigated. The results show that PVC/wood powder foaming materials, in which the wood powder is trcated by siloxane coupling agcnts and its particle size is 117 μm ( i. e. 120 mesh), has good comprehensive propertices, the dcnsity of PvC/wood powder foaming material incrcases with the incrcase of wood powdcr dosagcs at presence of the same dosagc of foaming agents, while the foaming ffects become bad.
木塑复合发泡材料是当前的研究热点，其符合环保的理念。木塑复合发泡材料以回收的废塑料和废木材为原料，对减少环境污染、保护森林资源意义重大。木粉填料（就木塑行业面言，包括木粉、竹粉、稻壳粉等各种植物纤维)的加入使材料具有木材的外观和颜色；发泡剂的加人使PVC/木塑发泡材料的密度更接近木材；同时，PVC/木塑发泡材料的防火、防潮、防蛙及隔音性能也大大优于传统木材1-2)。
笔者主要考察了木粉的性能对PVC/木塑发泡
材料性能的影响。 1试验部分 1.1主要原料
PVC树脂，S-700，中国石油化工股份有限公司齐鲁分公司；ADC发泡剂，AC3000，杭州海虹精细化·［收稿日期］2010-07-20
工有限公司；加工助剂，ACRZB-530，消博华星助剂有限公司；钙锌复合稳定剂，R8965，德国BAER-
LOCHER有限公司；木粉及其他助剂，市售。 1.2主要仪器和设备
PVC专用混合机组，SRL-Z.张家港市万塑机械有限公司；单螺杆挤出机，德国Brabender公司；微机控制电子万能试验机，WPW-20C，上海华龙测试仪器公司；显微镜，DMLT，德国莱卡公司；密度仪，D-H100，日本东洋精机株式会社；热重仪，2950，美国TA 公司。
1.3测试方法
①拉伸强度及断裂伸长率按照GB/T1040-2006《塑料拉伸性能的测定》检测，拉伸速度20 mm/min。②冲击强度按照GB/T1043一2008《塑
［作者简介］贾小波（1978一），男，工程师，2002年毕业于沈阳化工学院高分子材料与工程专业，现从事PVC配方研发
工作。 24