第39卷第9期
2011年9月【加工与应用】
聚氯乙烯 Polyvinyl Chloride
模具对PVC型材性能的影响
汪进南”
（安微广德金鹏新材料制造有限公司，安徽广德242200）
[关键词］PVC型材；模具；压缩比；长径比；性能
Vol.39,No.9 Sep.,2011
[摘要］考察了PVC型材模具的长径比、压缩比及长径压缩比对产品拉伸强度、断裂伸长率、冲击强度、受压弯曲应力的影响。结果表明，所考察的模具较合适的压缩比为3.6左右，长径比为40左右。
［中图分类号］TQ325.3;TQ320.66*3
[文献标志码］B
［文章编号】1009-7937(2011)090024-04
Influences of mould on properties of PVC profiles
WANGJinnan
( Anhui Guangde Jinpeng New Material Manufacture Co., Ltd., Guangde 242200, China) Keywords:PVC profile; mould; compression ratio;ratio of hcight to diameter;propcrty Abstract: Influences of the length-to-diameter ratio, compression ratio and ratio of length-to
diameter-ratio to compression-ratio of mould for PVC profiles on the tensile strcngth, clongation at break, impact strength and compressive bending stress of products were investigated.The rcsults showed that the suitable compression ratio and length-to-diameter ratio for studied mould wcre a-bout 3.6 and 40,respectively
在PVC型材的挤出过程中，模具的尺寸规格对
PVC型材的生产稳定性及内在质量有重要的影响。笔者就模具的压缩比、长径比等方面进行试验，并对试验结果进行简要分析。
1试验部分 1.1配方
PVC型材的试验配方见表1。
表1PVC型材的试验配方
Table1Test formula for PVC profiles
原料 PVC 稳定剂 o TiO2 ACR CPE 润滑剂
鲁属 SG5 303
轻质、活性，粒径18μm
R105 401 135A
1.2设备与模具
用量/份 100 4.5 5~10 5~8 1~2 6~8 0.2~0.5
SL500-1000型热冷混料机组，江苏某公司；65，［收稿日期］2010-12-08
-132型锥型双螺杆挤出机组，上海某公司；XYZ 12型哑铃型制样机、XWW-20型拉伸试验机、XJI-5型简支梁冲击强度测试机，承德市金建检测仪器有限公司；模具（共10套），80推拉框，铜陵三佳
科技股份有限公司。 1.3试验流程
配料→110℃热混→45℃冷混→+挤出成型→
切割取样→+制样→+测试。 1.4挤出参数设置
油温75℃，料筒1区176℃，料筒2.区180℃，料简3区168℃，料简4区165℃，合流芯160℃，模具1区185℃，模具2区195℃，模具3区195 ℃，模具4区195℃，模具5区195℃，挤出速度2.2 m/min。
1.5模具测试
(1)口模处各端面壁厚；A,、A2、A,...A.，平均值为A。
［作者简介］汪进南（1984一），男，2007年毕业于合肥工业大学高分子材料与工程专业，从事PVC型材的挤出工艺及
配方工作。万方数据