郭志刚，梅园，张峰博，陈飞
（天能集团研究院，浙江长兴313100）
摘要：木素磺酸钠是常用的有机膨胀剂。使用本素磺酸钠作为负极板膨胀剂的在化成时，经常有AGM隔板变色现象。利用SEM/XPS等分析方法对变黄物质进行了表征，结果表明，该黄色物质应该是水素确酸钠的降解产物。
关键词：铅酸蓄电池；负极板；铅膏；木素磺酸钠；有机膨胀剂；电池化成；AGM隔板；隔板变色
中图分类号：TM912.9
文献标识码：A
文章编号：1006-0847(2016)06-283-04
ResearchonthecolorchangeofAGMseparatorsduring
containerformationoflead-acidbatteries
GUO Zhigang, MEI Yuan, ZHANG Fengbo, CHEN Fei
(The Academy of Tianneng Group, Changxing Zhejiang 313/00, China)
Abstract: Sodium lignosulphonate is an organic expander commonly used in the negative plate of lead-acid battery. The color of some AGM separators adjacent to the negative plates was changed from white to yellow during container formation of lead-acid batteries used sodium lignosulphonate as negative expander. By scanning electron microscope and X-ray photoelectron spectroscopy, it turned out that the yellow materials might be the degraded products of sodium lignosulphonate.
Key words: lead-acid battery; negative plate; lead paste; sodium lignosulphonate; organic expander; container formation; AGM separator; color change of separator
0引言
在铅酸蓄电池负极板配方中，一般含有有机膨胀剂，而木素磺酸钠则是铅酸电池中常用的有机添加剂之一]。木素磺酸钠的分子量分布极不均匀，结构复杂，功能不一，含有一定的酸性基团，通常以电解质的形式存在，具有胶体性质。木素磺酸盐在水溶液中呈现出阴离子聚电解质的特性，在酸性
收稿日期：201604-12 万方数据
条件下木质素分子倾向于缔合形成共聚物，在碱性条件下则比较稳定。木素磺酸钠具有良好地分散性、粘结性和表面特性2，在电化学应用领域，主要应用在电镀行业和铅酸电池中。含有木素磺酸钠的负极铅膏在和膏过程中，加水后木素磺酸钠能明显起到分散剂的作用，降低错营的黏度，便于膨胀剂和铅粉充分混合均匀3。此外，含有木素磺酸钠的负极板固化干燥后极板脱粉的机率降低，这是木素磺酸钠具有粘结性的体现。添加木素磺酸钠的负极板在放电过程中会在铅金属表面形成一层胶状的三维网状结构，该网状结构可以允许Pb2+穿过，使得硫酸铅在这层膜上形成，不会覆盖在极板上使极