战祥连，唐胜群，陈龙霞，新树峰，吴海
（淄博火炬能源有限责任公司，山东淄博255056）
摘要：通过测试富液式铬酸电池在不同充电温度下的负极析氢电位，分析不同状态下隔板的显微照片和充电期间的电压变化，对3种PE隔板进行比较研究发现：C型隔板在30℃对锑离子的阻档效果最好；A型隔板在50C对锑离子阻档效果最好。上述现象与隔板在不同状态下的扎率、扎径变化有直接关系。
关键词：富液式铅蓄电池；PE隔板；锦离子：迁移率：负极；析氢电位：孔率；扎径
中图分类号：TM912.1
文献标识码：B
文章编号：1006-0847(2018)04-167-04
Theeffects of PE separators on antimony ion mobilityin
floodedlead-acidbatteries
ZHAN Xianglian,TANG Shengqun,CHEN Longxia, JIN Shufeng,WU Tao
(Zibo Torch Energy Co., Lid., Zibo Shandong 255056, China)
Abstract: By testing the hydrogen evolution potential with LSV method and analyzing the microscopic images of separators under different conditions and the voltage changes during the charging process at different charging temperature, three types of PE separators are compared and studied. The results show that the antimony ion mobility is low respectively when the type C of PE separators are used at 3o C, and the type A of PE separators are used at 50 C, which is directly related to the porosity and pore diameter of PE separators under different conditions
Keywords: flooded lead-acid battery; PE separator; antimony ion; mobility; negative electrode; hydroger evolution potential; porosity; pore diameter
0引言
由于功率密度大，成本低，富液式铅酸蓄电池在叉车等动力领域仍被广泛应用着！。在深循环富液式铅酸蓄电池中，正板栅普遍采用铅锑合金。锑的加入提高了合金的机械性能，但同时也影响正极的电化学性能，在阳极条件下，合金中的锑元素易
收稿日期：2017-12-12*通信作者
万方数据
被正极的二氧化铅氧化成Sb的三价物质，进而造成正极板栅的腐蚀，其在充电过程中发生的形态变化如下：
Sb→SbOH,→SbO→SbO+/SbOSO,/Sb(OH)SO,。
根据充电电压的高低，在正极附近产生的 Sb+、Sbs+离子的浓度不同。由于在电解液中，锑离子会受到浓度差的作用而产生扩散，因此锑离子容易穿过隔板中的微孔扩散到负极。到达负极的锑离子会吸收来自负极的电子，发生逆反应，重新生成锑单质，分布在负极活性物质表面，与海绵状铅形成微电池，产生局部自放电，使电池容量下降。同时，锑的大量沉积，会降低负极氢的析出过电