电池化成充电技术的研究与探讨
牛义生，陈志雪，李亚辉，张志伟，任建华（风帆股份有限公司，河北保定071057）
摘要：根据电极活性物质结构特点及其在化成充电过程中的反应特性，试验研究提高电池化成中的电流密度，缩短充电时间，实现快速化成。并通过实例，验证了提高电流密度对电池化成过程及电池性能的影响。
关键词：铅酸蓄电池；快速化成：电流密度：蓄电池性能；电池化成
中图分类号：TM912.1
文献标识码：B
文章编号：1006-0847(2014)01-41-04
Researchanddiscussiononthechargingtechnologyof
containerformation
NIU Yi-sheng, CHEN Zhi-xue, LI Ya-hui, ZHANG Zhi-wei, REN Jian-hua
(Fengfan Co., Ltd., Baoding Hebei 071057, China)
Abstract: According to the structural characteristics and the reaction characteristics of the active material in the formatting process, the curent density during the container formation was increased and the charging time was shortened in the experiment, in order to realize the quick formation. And through an example, the effects of the increase of current density on the formation process and performance of lead-acid battery were verified.
Key words: lead-acid battery; quick formation; current density; battery performance; container formation
0前言
随着国家产业政策的调整，电池化成技术在铅酸蓄电池领域得到了广泛的推广和应用。电池化成（也称内化成）技术具有污染小、三废排放低、生产方便等优点，然而，电池化成也存在差生产周期长、占用空间大、生产效率低等不足，是当今业界
收稿日期：2013-07-29
一直关注和有待解决的问题。因此，缩短电池内化成时间，实现快速化成具有非常重要的现实意义。
1铅酸蓄电池电极及其反应特性
生极板组装的铅酸蓄电池，其正、负电极上的
活性物质主要是由碱式硫酸铅、氧化铅及少量的钳和水分组成，经过前期的固化干燥，水分蒸发，便得电极上活性物质内部生成许多孔隙，有很大的比表面积，这有利于降低真实电流密度，降低电化学极化。在加液后的充电过程中，从电化学反应的平衡电势来看，氧化铅、碱式硫酸铅及铅的反应电势低于硫酸铅，会优先于硫酸铅在电极上进行电化