Ba掺杂的Pb-Ca-Sn-Al合金性能的研究
赵弟，牛义生，杨占欣，宋志光，荣琳，闫楠楠
（风帆责任有限公司，河北保定071057）
摘要：本文对不同领含量掺杂的Pb-Ca-Sn-A1合金的机械性能、电化学性能以及耐腐蚀性能进行了研完。研究结果表明，在合金中掺入适量的锁，在一定程度上可以提高合金的抗拉仲强度
以及扇蚀膜的导电性，但是锁的加入会使析氧过电位降低，合金的耐离蚀性下降。关键词：铅酸蓄电池；铅合金；领；抗拉伸强度；腐蚀膜导电性；析氧；耐腐蚀性
中图分类号：TM912.1
文献标识码：B
文章编号：1006-0847(2016)04-171-04
Thestudvofbarium-dopedlead-calcium-tin-aluminumallovs
ZHAO Di, NIU Yisheng, YANG Zhanxin, SONG Zhiguang, CHAI Lin, YAN Nannan
(Fengfan Co., Ltd., Baoding Hebei 071057, China)
Abstract: In this paper, the performances including mechanical properties, electrochemical properties and corrosion resistance of lead-calcium-tin-aluminum alloys doped with different contents of barium are studied. The results indicate that the tensile strength and corrosion film conductivity are improved to some extent if lead-calcium-tin-aluminum alloys are doped with appropriate amount of barium However, barium will decrease the overpotential of oxygen-evolution, then the corrosion resistance of alloys is decreased.
Key words: lead-acid battery; lead alloys; barium; tensile strength; corrosion film conductivity; oxygen evolution; corrosion resistance
0前言
板栅材料的好坏对铅酸蓄电池的使用寿命起着至关重要的作用l-2]。Pb-Ca-Sn-Al合金凭借自身的优点已逐步取代Pb-Sb合金广泛用作铅酸蓄电池板栅材料，但其仍存在机械性能差、钝化现象严重以及耐腐蚀性能差等问题3-引)。因此，改善现有合金的性能是目前研究的热点之一，其中，掺杂其它金属
元素到合金中是改善合金性能有效方法之一[6-1] 收稿日期：201605-18
本文在Pb-Ca-Sn-A1合金中添加了不同含量的 Ba，并对其机械性能、电化学性能以及耐腐蚀性能进行了研究，探讨了Ba作为Pb-Ca-Sn-A1合金添
加剂对合金综合性能的影响。 1实验
1.1合金材料
为了研究Ba添加剂对正板栅用Pb-Ca-Sn-A1 合金性能的影响，实验配制了几种不同Ba添加量的合金，见表1。由于合金的元素组成对合金的性能影响很大，本实验对几种合金的含量进行了严格的控制。为了便于研究其性能，将下述合金浇铸形成相同规则形状的样条。
2016 No.4 Vo1.53171