电化学等综合测试方法在铅酸蓄电池失效解
剖分析上的应用研究史俊雷，张祖波，张行祥，夏诗忠，刘长来
（骆驼集团蓄电池研究院有限公司，湖北襄阳441000）
摘要：通过综合应用各种分析测量工具，如电化学、XRD、SEM等，对铅酸蓄电池失效模式的根本原国进行分析，为以后的电池性能改进提供更精准的研究方向，避免研究方向的错误，节省研发时间、提高研发效率。
关键词：铅酸蓄电池；失效模式；解分析；电化学；XRD；SEM；离蚀层；活性物质
中图分类号：TM912.9
文献标识码：B
文章编号：1006-0847(2016)06-295-04
Study ontheapplication of comprehensivetestmethods
inthefailuremodeanalysis oflead-acidbatteries SHI Junlei, ZHANG Zubo, ZHANG Xingxiang,XIA Shizhong, LIU Changlai
(Hubei Camel Storage Battery Research Institute Co., Lid., Xiangyang Hubei 441000, China)
Abstract: By use of the comprehensive application of various analysis measurement tools, such as electrochemistry, XRD, SEM, etc., to analyze the fundamental causes of the lead-acid battery failure modes and provide more accurate direction for battery performance improvement to avoid the research work from wrong direction, thus saving time and raising the efficiency of R&D
Key words: lead-acid battery; failure mode; dissection; electrochemistry; XRD; SEM; corrosive layer active material
0引言
目前铅酸蓄电池行业对失效电池的解剖分析一般仅局限于失效模式上的判断，如正极活性物质的软化，负极的硫酸盐化等，而缺少对失效原因的进行进一步分析。本项目通过对极板自身电化学特性、正负极工作电位及其它综合分析手段（如 SEM、XRD等），分析电池失效模式产生的根本原因，为改善电池的性能提出更有针对性的依据。