Φ40mm螺纹钢横肋裂纹的分析与控制
刘振
（河钢集团宣钢公司二钢轧厂，河北宣化075100）
Total No. 260 2017,Number8
摘要：分析了500BΦ40mm钢筋在生产过程中出现的横助末端微裂纹产生的原因。通过对相关铸坏进行表面质量、低倍组织及金相组织检验，认为连铸二冷水冷却不均匀形成了铸坏环角部裂纹，经轧制后导致了钢筋微裂纹的产生。通过调整二冷水冷却工艺参数和喷淋管角度、优化钢筋孔型等措施，消除了
500BΦ40mm螺纹钢的表面微裂纹。关键词：螺纹钢；横助；裂纹；分析；控制
中图分类号：TG335.6
文献标识码：B
doi:10. 13630/j. cnki. 13 1172.2017.0816
文章编号：10065008（2017)08005504
ANALYSISANDCONTROLOFCROSS
RIBCRACKONΦ4OmmREINFORCEDBAR
Liu Zhen
( No. 2 Steel Rolling Mill, Xuansteel Company, Xuanhua, Hebei, 075100)
Abstract : The reasons for micro cracks on the end of cross rib in production of 500B p 40 mm reinforeed bar are analyzed. It is considered that the corner cracks of casting blank are caused by uneven cooling of seconda-ry cooling, which is resulted in the micro crack of steel bar after rolling. with the inspection of surface quali ty, macrostructure and metallographic structure of the billets, The surface micro cracks of 500B 40 mm steel were eliminated by adjusting the parameters of the cold water cooling process and the angle of the spray pipe and optimizing the pass of the steel bars.
Key Words : reinforced bar; cross rib; crack; analysis; control
引言
随着社会的不断发展，更高强度、更高性能稳定
性抗震钢筋的用途越来越广泛，尤其核电站、超高层建筑等重点工程对高级别大规格抗震钢筋的需求更是强烈，因此提高大规格高强钢筋的质量和性能更为迫切。Φ40mm热轧直条螺纹钢作为其中的一个代表品种，具有较大的断面尺寸，在高层建筑、桥梁建筑及重要的基础设施建设中得到了广泛应用。
按照热轧带助钢筋的国家标准（GB1499.2-2007）规定，钢筋表面应无有害的表面缺陷和受弯曲部位不得产生裂纹。宣钢公司二棒生产线生产的 500BΦ40mm钢筋在质量检查中，发现个别钢筋
收稿日期：2017-04-21
作者简介：刘振（1981－），男，工程师，2005年毕业于河北理工大学金属材料工程专业，现在河钢集团宣钢公司长期从事轧钢生产工艺、质量控制工作，Email:liuzhen9807@163.com
万方数据
横肋位置出现了不规则裂纹。经检测，裂纹未扩展到基圆直径，弯曲试验后也未向四周放散，也未对螺纹钢质量和性能产生影响。为进一步提高高强抗震钢筋的质量，需要研究横助裂纹产生的原因，并采取相应的控制措施。
1
生产工艺
宣钢公司二棒生产线Φ40mm钢筋由150t炉
区供料，钢坏断面尺寸为165mm×165mm，炼钢工艺：转炉炼钢一LF炉精炼一→连铸。该生产线全线有 18架轧机，平立交替布置，Φ40mm螺纹钢生产采用12架轧机其中11架、12架空过，14架出成品，其轧制工艺流程如图1所示。
55