模具技术2016.No.1
文章编号：1001-4934(2016)01-0043-04
Φ89mm连轧管机组钢管内孔不圆原因分析
张迎春1,2，夏挨达'，陈平1
（1.湖南财经工业职业技术学院机电工程系，湖南衡阳421002
2.衡阳华菱钢管集团有限公司，湖南衡阳421001）
43
摘要：对Φ89mm连轧管机组生产中出现的几种典型钢管内孔不圆的成因进行了分析，分析了钢管壁厚不均的产生原因，确定了钢管内孔不圆的本质是钢管壁厚不均。通过提高荒管壁厚精度、工模具精度、再加热温度均匀性和改进张减机工艺参数等指施，能够有效地改善钢管内孔不圆程度。
关键词：内孔不圆；成因分析；横向壁厚不均
中图分类号：TG355
文献标识码：B
Analysis of inner hole out of round for 89 mm pipe continuous rolling mill
ZHANG Ying-chun, XIA Kui-da, CHEN Ping
Abstract:Thereasons for several typical problemsthat innerhole is outof roundproducing by 89 mm pipe continuous rolling mill are analyzed. And the causes of uneven pipe wall thickness are studied. It is found that the pipe inner hole out of round is due to the uneven wall thickness. By increasing pipe wall thickncss accuracy, dic prccision, reheating temper-ature uniformity and improved machine process parameters,the roundness level of steel pipe inner hole can be effectively improved.
Keywords: inner hole out of round; cause analysis; transverse uneven thickness
109mm孔型。为了适应市场需求，该分厂将
0引言
某公司89mm分厂半浮芯棒连轧管机组主体设备从德国曼内斯曼-米尔公司引进，包括二辊锥形穿孔、半浮芯棒连轧管机、24机架集中差速-串联张力减径机三大主机。主要工艺路线为：环形炉加热→+穿孔→连轧→步进炉再加热 →高压水除磷→张力减径，该机组原工艺设计范围：25~89）mm×2.5~12mm，连轧机为
轧制规格范围扩大：连轧机孔型增加了4套，分别为95mm孔型、126mm孔型、133mm孔型、Φ139mm孔型，壁厚系数范围达到0.03≤ S/D≤0.25，轧制规格达到（32~37）mmX3.5 ～16mm。随着89mm分厂生产组距的不断扩大和主体设备的不断老化以及所生产钢管的壁厚系数的提高，使得在实际生产中出现了一些钢管质量问题，特别是在生产直径60mm， S/D≥0.15的小口径厚壁管时，经常出现钢管
收稿日期：2015-08-10
基金项目：衡阳市科技局工业支撑计划项目衡科发（2012KG82)。作者简介：张迎春（1967一），女，副教授。