总第211期 2016年8月
文章编号：1009~9700(2016)04003704
南方金属 SOUTHERNMETALS
板坏连铸机包晶钢结晶器液面
波动原因分析及控制
王冠，刘志明
（宝钢集团广东韶关钢铁有限公司，韶关广东512123）
Sum.211 August2016
摘要：韶钢板坏连铸机生产包晶钢时结晶液面波动间题较突出，液面波动炉次发生比例22.78%，导致铸坏表面裂纹及夹杂缺陷量上升，影响产品质量.文章对韶钢板坏铸机液面波动原因进行分析，提出了在液面控制系统、保
护渣性能、冷却制度等方面采取相应控制措施，改善包晶钢液面波动情况，确保生产的稳定性与连续性关键词：板坏连铸：包晶钢；结晶器；液面波动
中图分类号：TF713
文献标识码：B
AnalysisandControlofMoldLevelFluctuationofContinuous
Slab Caster during Peritectic Steel Casting
WANG Guan,LIUZhi-ming
(Steelmaking Plant of Baosteel Group Guangdong Shaoguan Iron & Steel Co. , Lid. , Shaoguan, Guangdong,512123, P. R. China)
Abstract : Mold level fluctuation of slab caster in SGIS is more prominent during peritectic steel casting, the ratio of liquid surface fluctuation is 22. 78%, resulted in increasing surface cracks and inclusion defects of slabs, which impact the prod uct quality. The causes of the level fluctuation are analyzed, appropriate countermeasures are applied for the liquid level control system, lubrication powder property, secondary cooling process and so on, which improve the level fluctuation dur-
ing peritectic steel casting and ensure the stability and continuity of production Key words : slab casting; peritectic steel; mold; level fluctuation
连铸过程中要求将结晶器液面波动控制在一定范围内（一般为±3mm），液面波动过大将会影响结晶器保护渣的三层结构，破坏其润滑和传热平衡，导致铸坏表面产生缺陷.同时也会增加结晶器钢水的卷渣风险，致使铸坏内夹杂物含量超标，严重影响钳坏和最终产品的质量，基至会造成铸坏纵裂钢、夹渣漏钢的恶性生产事故[].因此，解决结晶器液面波动大的问题对连铸机正常生产和铸坏质量控制非常重要，
1连铸机主要工艺参数
宝钢集团广东韶关钢铁有限公司（以下简称“韶钢”）板坏钢种主要生产工艺流程为：BOF-→LF 收稿日期：2016-02-15
+CC或BOF→LF-→RH→CC.目前有一机—流板坏连铸机2台，其中4号连铸机的主要工艺参数见表1.
2问题的提出
韶钢板坏连铸易出现液面波动钢种主要为碳素结构钢，液面波动的发生存在偶然性，波动幅度±15 mm，常见液面波动控制曲线如图1所示.一般连铸只能降低拉速浇钢，不能消除液面波动发生，直接影响浇注，并极易引起铸坏裂纹、夹杂等缺陷.生产的碳素结构钢多数属于包晶钢范围，其化学成分见表2.
作者简介：王冠（1987-），男，2010年毕业于武汉科技大学冶金工程专业，助理工程师，