降低板坏连铸结晶器卷渣的措施
魏艳龙'，王静”
Total No.249 2016,Number9
（1.河钢集团邯钢公司质量检验部，河北邯郸056015；2.河钢集团邯钢公司邯宝炼钢厂，河北邯郸 056015
摘要：从降低结晶器液面波动人手，选取了3个有代表性的测量点，研究了不同拉速条件下，不同的水口结构和水口插人深度对液面波动高度的影响，确定了适宜的浸人式水口结构和水口浸人深度范围。应
用后，降低了结晶器卷渣机率和热轧卷板的边部缺陷。关键调：连铸；结晶器；卷渣：浸人式水口；液面波动
中图分类号：TF341.6
文献标识码：B
doi;10. 13630/j. cnki. 13 1172. 2016.0913
文章编号：10065008(2016)09004704
MEASURES TO IMPROVE SLAG
ENTRAPMENTONMOLDOFSLABCASTER
WeiYanlong',Wang Jing
(1. Quality Detection Department, Hesteel Group Hansteel Company, Handan, Hebei, 056015; 2. Hanbao Steelworks, Hesteel Group Hansteel Company, Handan, Hebei, 056015)
Abstract; To lower the liquid fluctuation height in mold, three representative measuring points are selected, the influence on the height of different nozzle structure and nozzle immersion depth under different casting speed is researched, and the suitable structure and depth range are determined. After all of these applied, the aaeeaeaaaeeeeee
Key Words; continuous casting; mold; slag entrapment; submerged nozzle; liquid fluctuation
引言
邯钢邯宝炼钢厂2台板坏连铸机由意大利达涅
利公司总体设计，浇铸断面230mm×（900~2150） mm，立弯式双机双流。从2012年10月份开始，热轧卷板出现边部裂纹缺陷，形态呈不规则断续条带状,尾部呈M型舌状裂纹，轧制薄规格卷板时有时存在翘皮缺陷。通过对大量铸坏取样酸洗检验发现，铸坏角部并没有裂纹，而对轧卷缺陷部位取样化验发现有保护渣的成分。究其原因，随着拉坏速度的提高，从SEN水口流出的钢水流速随之提高，从而引起结晶器弯月面动的加剧，结晶器液面的熔融保护渣和钢渣卷人钢水中的机率随之增加，最终在轧制卷边后形成边部裂纹缺陷。
1
边部缺陷宏观形貌
收稿日期：2016-0718
作者简介：魏艳龙（1975-），男，工程师，2008年毕业于北京科技大学冶金工程专业，现在河钢集团邯钢公司质量检验部工作，E-mail
weiyanlong@ mail. hgjt.cn 万方数据
卷板边部缺陷的宏观形貌如图1所示。
图1轧材边部缺陷的宏观形貌
Fig.1
Macro morphology of edge defects on rolling pieces 结晶器卷渣机理
大量文献研究[1.2]表明，卷渣主要有5种类型：(1)结晶器窄面钢液表面回流引起的稳定的卷渣：(2)水口附近的漩涡卷渣；（3)吹氩过程的上升气泡引起的卷渣；（4）结晶器窄面钢液表面回流引起的非稳定的卷渣：（5）沿着水口方向的压力差引起的非稳定的卷渣。而这5种类型的卷渣方式都与结晶器的液面波动行为和表面流速密切相关。
本文针对邯钢的实验操作过程进行总结分析，
47