X60钢非金属夹杂的控制措施
孙作迎，李强刚
（日照钢铁控股集团有限公司，山东日照276806）
Sum.208 February 2016
摘要：综合日钢X60钢生产现状，对A类、B类夹杂变性进行分析.认为，钢液内ACR应>1.8的条件，可满足A 类夹杂完全变性；通过钢液内T[O]变化，预知B类夹杂相对数量，以达到[Ca]/[AI]>0.14,可达到B类夹杂完全
变性.如何有效降低C类夹杂，需进一步探讨论证关键词：X60；夹杂；措施
中图分类号：TF704.7
文献标识码：A
ControlMeasuresforNonMetalInclusionsofSteelX60
SUN Zuo ying, LI Qiang gang
(Rizhao Steel Holding Group Co, , Lad. , Rizhao, Shandong, 276806, R. P. China)
Abstract: Aiming at the comprehensive situations of making steel X60, inclusion modifications of types A and B were ana lyzed. It is considered that if ACR in steel is greater than 1. 8, it can meet the complete modification of type A; the relative inclusion quantity of type B can be predicted by the T[ O] change in steel in order to achieve that the [ Ca]/[ Al]is greater than 0. 14 which can make the complete inclusion modification available, It is necessary to be further discussed on how to
reduce the inclusion of type C effectively Key words: X60; inclusion;measure
0前言
钢中夹杂物的形态控制是高级别管线钢生产的关键技术(1).本文主要针日照钢铁控股集团有限公司（以下简称“日钢"）BOF-LF-CC工艺生产X60 钢,讨论了钢液T[O]、钢液[S]和钢液[Ca]对夹杂物形态控制的重要性，尤其是对MnS和Al,O，夹杂物的形态控制.通过生产过程中的取样分析，综合评价得出降低X60钢非金属夹杂的工艺措施
1工艺流程及控制要点 1.1工艺流程
BOF-LF-CC工艺生产X60钢的工艺流程如下：
铁水喷镁脱硫→120t顶底复吹转炉→转炉出钢脱氧合金化→LF精炼→+钙处理→+弱搅拌→60t
中间包一→+直弧形板坏连铸机，收稿日期：2015=09=06
1.2控制要点
BOF-LF-CC工艺生产X60钢工艺控制要点见表1.
2
结果与评价
2.1试验结果
生产X60钢共计18炉，第2炉，B级细系夹杂物等级为2.5S级；第3炉，A级细系夹杂物等级为
2.5级.第2、3炉化学成分见表2. 2.2降低A类夹杂的工艺措施
根据文献[2].提出用原子浓度比ACR来衡量
A类夹杂变性程度的指标，当钢液w（Ca）为（20~ 50）×10-‘时，根据公式（1）可计算出ACR控制范围
ACRc.=(Ca)-(0.18+130a(Ca)) :(0)
1.25×w(S)
(1)
作者简介：孙作迎（1982-），男，2006年毕业于河北理工大学冶金工程专业，助理工程师