ICP-OEC测定低碳微碳铬铁中的微量钒和钻
弥寒冰
（攀长钢技术中心理化检测中心，四川江油，621701）
Vol.20(80) 2014.No.3
摘要：采用电感揭合等离子体原子发射光谱法(ICP-OES)对低碳微碳铬铁中截量钒和钻进行了分析测定。本试验对分析谱线、基体效应、酸度、仪器参数等方面进行了研究，并确定了低碳微碳铬铁中微量钒和结测定的最住仪器分新参数。进行了准确度、精密度分析试验及样品检验，结果满意。
关键词：ICP-OES；低碳微碳铬铁；；钻
中图分类号：TG115.3+3
文献标识码：A
文章编号：16740971(2014)03046~03
DeterminationofTraceAmountofVanadiumandCobaltin FerrochromiumwithLowCarbonorMicroCarbonby
InductivelyCoupledPlasmaAtomicEmissionSpectrometry
Mi Hanbing
(Jiangyou Changcheng Special Steel Co., Ltd., Pangang Group, Jiangyou, SiChuan, 621701)
Abstract: Trace amount of vanadium and cobalt in ferrochromium with low carbon or micro carbon was analyzed and determined by inductively coupled plasma atomic emission spectrometry method(ICPOES).The analysis spectral line, matrix effect, acidity, instrument parameters were studied and the best instrument analysis parameters for
determination of trace vanadium and cobalt in ferrochromium with low carbon or micro carbon were determined in the test. The aceuracy, precision analysis test and sample test were conducted with satisfactory results.
Keywords: ICPOES, Low carbon miero carbon ferrochromium, Vanadium, Cobalt
钢中残余元素含量的高低往往由冶炼所用原
材料带入。对冶炼所用原材料中残余微量元系作准确分析,是准确控制钢中残余微量元素含量的重要保证。
低碳微碳铬铁是特钢冶炼所用主要原材料，按标准及验收要求，只分析Cr,P,Si,C,S主量元素。目前，没有分析低碳微碳铬铁中残余微量元素V、Co 的国家标准分析方法，因此，需研究开发能准确测定低碳微碳铬铁中残余微量元素V、Co含量的分析方法。
电感耦合等离子体原子发射光谱法(ICP-OES) 具有分析精度高、速度快、干扰小、检出限低、线性范围宽、可进行多元素同时测定等优点[1,2]目前已在分析测试中广泛使用。为了更好地适应我公司产品开发、科研及生产需求，本文对应用ICP-OES 法，对测定低碳微碳铬铁中残余微量元素V、Co的分析方法进行了研究试验，确定了最佳试验条件，
收件日期：20140913
修日期：20140917
建立了分析方法。本方法分析结果准确可靠，满足了我公司生产及科研需要。
试验部分 1
1.1主要仪器及条件
美国PE公司Optima5300DV型ICP-OES，频率 40.68MHz
功率：1250W；等离子体流量：15L/min；雾化气流量：0.70L/min；辅助气流量：0.2L/min；样品提升量：1.7mL/min；观测方式：垂直；冲洗时间：30s；积分
时间：55。 1.2试剂
盐酸（p1.19g/ml,)优级纯：高纯水(18MQ·cm）；
硫酸（p1.84g/ml)：优级纯；磷酸（p1.69g/ml）：优级纯
高纯金属：纯度大于99.99%；
作者简介：弥寒冰，女，四川江油人，责任技师，2001年毕业于北京科技大学计算机管理工程工作，长期从事化学分析专业，供职于举钢集团江油长域股份有限公司技术中心理化检测中心。Tel:(0816)3648837;Ema11;362081557@qq.com