固化工艺和正负极配比对电池性能和寿命的影响
蒋忠华，胡义春，方明学，杨惠强
（浙江天能电池（江苏）有限公司，江苏沭阳223600）
摘要：本文试验了正极板不同的固化工艺、正负极不同的活性物量和极板数量配比，对电动车电池初期性能和寿命的影响，得出了采用正板包负板的极群结构可明显提高电池寿命的结论。关键词：电动车电池；极板；活性物；固化；初期性能；循环寿命
中图分类号：TM912.1
文献标识码：B
文章编号：1006-0847(2015)02-83-04
Theimpactofcuringprocessandproportionofpositiveandnegative
plates on theperformance and cycle life of lead-acid battery
JIANG Zhong-hua', HU Yi-chun, FANG Ming-xue, YANG Hui-qiang
ZhejiangTiannengBattery (Jiangsu)Co.,Ltd.,Shuyang Jiangsu 223600, China)
Abstract: This paper studied the difference curing process of positive plates, the amount of active materials and the ratio between positive and negative plates, and also discussed their impact on the initial performance and cycle life of lead-acid battery. Finally it concluded that the structure of plate group can significantly improve battery's cycle life, in which the number of positive plates is one more than that of negative plates.
Key words: battery for electric vehicle; plate; active material; curing; initial performance; cycle life
0前言
电动车用铅蓄电池，多年来正极材料一直使用
对其性能和寿命都有保障的错锦镉合金，但辐对人体的危害很大，为保护环境，铅蓄电池已按环保要求进行了去镉化，无镉合金的使用对电动车电池的性能和寿命都是一个不小的考验。况且电动车电池经历多年的快速发展，已到了市场激烈竞争阶段，如何降低电池成本，提高电池质量，特别是如何提高电池寿命，从而提高市场竞争力，是许多技术人
收稿日期：2014-11-19*通讯联系人
832015 No.2 Vo1.52
员都在思考和研究的课题。
为此，我们以不同的固化工艺、不同的正负极活性物量的配比、不同的正负极板数量配比，对电池初期性能和寿命的影响进行了对比试验和分析，希望能加深认知，找到较佳的正负极活性物配比和
提高寿命的更多方法。 1试验内容
按正极板不同的固化工艺、正负极不同的活性物用量、不同的极板数量和装配结构，小量组装6-DZM-12电动车电池，详见表1。电池经充电配组后，各抽取两组，一组按GB/T22199-2008标准做初期性能检测，另一组模拟用户按100%DOD 做循环寿命测试（恒压14.8V/只，限流1.5A充电