固化充电工艺对稀土合金正极板性能的影响
戴德兵，张文泉，付定华，李忠明，乔卫建，刘长华
（旭派电源有限公司，江苏宿迁223800）
摘要：通过选用铅钙稀土新型合金和普通高锡合金，对采用不同固化、充电工艺生产出的生极板和熟极板进行扫描电镜分析和XRD测试，并对组装电池的容量和深循环寿命进行了比较试
验，以确定满足稀土合金用作动力电池这一深循环使用寿命特性的固化和充电工艺。关键词：固化；充电；铅钙稀土合金；正极板；动力电池；深循环
中图分类号：TM912.1
文献标识码：B
文章编号：1006-0847(2017)06-289-04
Theinfluencesof curingandchargingprocessontheperformancesof
rareearthalloypassiveplates
DAI Debing, ZHANG Wenquan, FU Dinghua, LI Zhongming, QIAO Weijian, LIU Changhua
(Xupai Power Co., Lid., Suqian Jiangsu 223880, China)
Abstract: By using SEM and XRD, the green plates and red plates with lead calcium rare earth alloy and ordinary high tin alloy were tested respectively, which were prepared under the different curing and charging processes. The capacities and deep cycle lives of the assembled batteries were compared to make sure the curing and charging processes which meet the requirements of rare earth alloy used in the power batteries
Keywords: curing; charging; lead calcium rare earth alloy:; positive plate; power battery; deep cycling
0引言
在中国，阀控式电池作为电动车动力电源已有二十多年。最初，正极板栅采用Pb-Sb-Cd合金：但是因该合金存在Cd污染问题，现在大多数厂家的动力电池正板栅采用Pb-Ca高锡合金。Pb-Ca高锡合金存在2个主要问题：1）板栅易腐蚀，及板栅表面腐蚀层在固化过程中难以形成，进而使板栅表面与活性物质结合力较差；2）正极板表面甚至极板深层产生泥化现象，使深循环放电难以持续进
收稿日期：2017-10-09
万方数据
行"。现在，大多数厂家通过添加SnSO。和Sb,O 等正极铅膏添加剂，使电池的深循环性能基本达到客户的要求，但随之而来存在长期过载放电的板栅腐蚀问题。如果选用耐腐能力强的Pb-Ca稀土合金，若固化效果不好，则泥化现象更为严重。基于此，我们对用作深循环放电的Pb-Ca稀土合金板栅的固化和充电工艺进行了深入的研究。
1制备样品 1.1生极板
分别选用表1中的合金1和合金2制备正板栅，在合金1中添加有少量Ag是为了增加板栅强度和细化晶核提高耐腐蚀能力；用合金3制备负板栅。用岛津式铅粉按正常和膏涂板工艺制成极板，