模具工业2017年第43春第9期
固溶温度对GH738合金环锻件组织性能的
影响研究
魏志坚，徐文帅，表慧，王龙祥，蒲思洪
（责州安大航空锻造有限责任公司，责州安顺561005）
摘要：针对GH738合金银件室温拉伸屈服强度不合格问题，采用热处理试验分析方法，研究了固落温度对GH738合金环锻件组织性能的影响，研究结果表明，在1000℃~1040℃，随着固溶温度逻渐升高，GH738环锻件室温拉伸屈服强度逐渐提高，其抗拉强度、延伸率和断面收缩率变化不大，提高固溶温度对GH738合金环锻件的品粒度影响不大，
关键词：固溶温度；GH738合金；组织性能；届服强度；抗拉强度
中图分类号：TG316
文献标识码：B
文章编号：1001-2168(2017)09-006305
DOI: 10.16787/j.cnki.10012168.dmi.2017.09.016
Effect ofsolutiontemperatureonmicrostructureandmechanical
properties of ringforgeablepiece for GH738alloy WEI Zhi-jian, XU Wen-shuai, YUAN Hui, WANG Long-xiang, PU Si-hong(Guizhou Anda Aviation Forging Co., Ltd., Anshun, Guizhou 561005, China)
Abstract: According to the unqualified of the tensile yield strength at room temperature of GH738 alloy, the effect of solution temperature on microstructure and mechanical proper-ties of it was studied by using heat treatment tests analysis. The results showed that the yield strength at room temperature of GH738 ring forgeable piece increased gradually with the solution temperature between 1 000 ℃ and 1 040 ℃, and there was a little change of the tensile strength, elongation and reduction of area. It could forecast that the solution temperature has a little influence on the grain size of GH738 ring forgeable.
Key words:solution temperature, GH738 alloy; microstructure and mechanical properties; yield strength; tensile strength
0
GH738合金锻件是以v相沂淀强化的镍基高温合金月，在760℃～870℃具有较高的届服强度和抗疲劳性能，在870℃以下的燃气涡轮中具有良好的抗氧化性和抗燃气腐蚀能力，该合金工艺塑性较好，组织稳定，广泛应用于航空、航天、石油、化工等领域。GH738合金锻件适用于制作涡轮盘、工作叶片、高温紧固件等零件，使用温度低于815℃2-4]。该合金主要通过固溶强化、相沉淀强化（主要为Ni3(A1,Ti))及碳化物强化等多种工艺的综合作用来达到强化效果。相是GH738合金锻件的主要强化
收稿日期：2017-06-12
作者简介：魏志坚(1970-)，男（汉族)，湖南隆回人，研究员级高级工程师，主要从事材料成型方面的工作。
万方数据
63
相，合金的性能主要取决于基体中相的百分含量、题粒大小和颗粒的粗化速率等5。董建新在参考文献[6]中指出,随若AI+Ti含量增加，合金中相的含量也从30%增加到50%，合金的抗拉强度和届服强度均随着AI+Ti含量的增加而提高，但A1、Ti含量增加却使合金的塑性有所降低。CHANGKM等研究了冷却速度对Waspalov合金性能的影响，研究结果表明，提高冷却速度可以提高合金的强度，且与增加强化相含量提高强度的效果一致。
现针对GH738合金锻件室温拉伸届屈服强度不合格问题，从提高固溶温度方面来探讨固溶温度对 GH738合金锻件室温拉伸屈服强度和组织的影响，为GH738合金锻件的实际生产提供理论指导和参考依据。