第38卷第4期
2010年4月【科研与生产】
聚氯乙烯
Polyvinyl Chloride
消光PVC与PVC-SG3配合制备电缆料
渠伟，，沈海涛，事惠文，李承东
（武汉祥龙电业股份有限公司树脂厂研发部，湖北武汉430078)
[关键词］消光PVC树脂；电缆料；电性能：力学性能
Vol.38,No.4 Apr.，2010
[摘要】研究了在70℃阻燃PVC电缆料配方中，消光PVC树脂的用量对制品电性能和力学性能的影响，结果表明：消光PVC树脂的用量为50份时，试样的综合性能较好，且达到了GB/T8815—2008中规定的J-70PVC 电绩料的指标及加工厂家的要求：同时，电缆料的配方成本比全部采用消光PVC树脂降低了9.29%。
[中图分类号］TQ325.3［文献标志码］B［[文章编号］1009=7937(2010)04-0008-03
Preparation of cable materials by compositing extinction PVC resin and PVC-SG3
LIANGWei,SHEN Haitao,LI Zhongwen,LIChengdong
(DevelopmentDepartmentof ResinPlant，WuhanXianglongElectric Co.，Ltd.，Wuhan430078，China)
Key words: extinction PVC resin; cable material; electrical property; mechanical property
Abstract: Influences of dosages of extinction PVC resin on the electrical property and mechani-cal property of firc-retardant PVC products at 7o C were studied. The results showed that when the dosages of extinction PVC resin were 50 parts, the sample had good comprehensive properties, and could reach the indexes in GB/T 88152008 about J 70 PVC cable materials and satisfy the re quirements of processing plants,meanwhile,the formula cost of cable material was cut down by 9.29%compared with that composed of extinction PVC resin only
消光PVC树脂具有耐热性、耐寒性和耐油污性
好及弹性高等待点，因面被广泛应用于电线电缆、各种电气产品及汽车非金属配件等领域。武汉祥龙电业股份有限公司树脂厂（以下简称武汉祥龙）在研制光纤用70℃阻燃PVC电缆料的过程中进行了大量的试验：如改变PVC树脂型号（由PVC-SG3改为 PVC-SG2)、减少增塑剂用量、改变增塑剂种类、调整填充剂用量等，但产品均不能完全满足GB/T 8815一2008《电线电缆用软聚氟乙烯塑料》中-70 PVC电缆料的指标和加工厂家的要求。
在中试装置成功生产出消光PVC树脂后，武汉祥龙用消光PVC树脂全部替代PVC树脂生产J 70PVC电缆料，所得制品的各项性能均达到GB/T 8815一2008指标和加工厂家的要求。此后，武汉祥
［收稿日期］2009-10-16
龙又尝试采用PVC树脂与消光PVC树脂配合，利用消光PVC树脂的独特性能来改善电线电缆制品的性能和质量，同时也可降低生产成本。
1试验部分 1.1原料
消光PVC-1800、PVC-SG3型树脂，武汉样龙，共100份（其中消光PVC1800所占份数分别为0、10、30、50、70、100份共6个样，分别标记为 1*、2、3#、4*、5"、6"）；邻苯二甲酸二辛酯，中国石化金陵分公司，45份；稳定剂，河北某助剂厂，6 份；填充剂，当阳某填充剂厂，25份；其他助剂，市售，适量。
[作者介］渠伟（1971一)，男，工程师，1993年毕业于成都科技大学（现四川大学)塑料工程系，主要从事PVC加工
和应用研究及PVC产品售后服务工作。 8
万方数据