第39卷第12期 2011年12月
聚氯乙烯
Polyvinyl Chloride
消光PVC树脂合成与加工成型的研究
陈俊杰，吕颖琦
（浙江巨化股份有限公司电化厂，浙江衡州324004）
[关键调］PVC;消光；合成；加工
Vol.39, No.12 Dec.,2011
[摘要］研究了交联剂用量及加入方式、案合温度对PVC树脂消光性能的影响，以及挤出温度对PVC制品消光性能的影响；对比了采用普通PVC树脂加消光剂生产的制品与采用消光PVC树脂生产的制品的消光性能。结果表明：①消光PVC树脂最佳的生产工艺为交联剂用量在0.3份左右，聚合过程中交联剂采用连续加人的方式，聚合温度应根据PVC制品凝胶含量的需求进行设定；②当挤出机各段温度分别为130、145、150、155C，模头溢度为165C 时，PVC制品的消光性能最好；③与采用加消光剂的方式相比，采用消光PVC树脂生产的制品消光性能更好。
[中图分类号］TQ325.3
［文献标惠码】B
［文量编号1009=7937(2011)12-002503
ResearchonthesynthesisandprocessingofmattPvCresins
CHENJunjie,LUYingqi
(Zhcjiang Juhua Co.,Ltd., Quzhou 324004,China)
Key words: PVC; matt; synthesis; proccssing
Abstract; Influcnces of dosagcs and addtion way of crosslinking agcnts and polymcrization tem-perature on the extinction propcrty of PVC resins werc studied as well as the influences of extruding tcmpcrature on the cxtinction propcrty of PVC products. Thc cxtinction propcrty of products pro-duccd from common PVC resin fillcd with cxtinction agcnts was comparcd with that of products produced from matt PVC resins.The results showed that: the optimum production proccss for matt PVC rcsin was that the dosages of crosslinking agcnts wcre O.3 parts, crosslinking agcnts wcrc continuously added into thc systcm during polymcrization, and thc sctting of polymcrization tem-pcrature should basc on thc gcl contcnts in PVC products; ② PVC products with thc best cxtinction propcrty could be obtained when the temperature of die hcad was 165 C and the tempcrature of cach stagc of cxtrudcr was 130,145,150 and 155C rcspcctivcly; productsobtained frommatt PVC resins were bctter than that obtained through the addition of cxtinction agcnts.
近年来，随着PVC树脂由通用化向高性能化、专用化方向发展，其在包装、建材、车辆、家具、服装等领域的用量逐渐增加。应用于这些领域的PVC 制品需要具有较低的表面光泽，因而推动了消光 PVC树脂的发展"}。笔者研究了中试生产的消光 PVC树脂的消光性能、加工性能以及力学性能等，旨在进一步提高消光PVC树脂的质量，拓宽其应用领域。
［收稿日期］2011-04-08 工作。
万方数据
1试验部分 1.1原料
氯乙烯（VCM)，工业聚合级，质量分数99.9% 以上，浙江巨化股份有限公司电化厂羟丙基甲基纤维索（HPMC)，65SH50，日本合成化学有限公司；聚乙烯醇（PVA），KH20，日本合成化学有限公司；过氧化二碳酸二乙基已酯（EHP)，天津阿克苏诺贝尔过氧化物有限公司；过氧化新癸酸异丙苯酯
25