PVC-M管件的刚韧平衡
孙培培”，李静，刘容德，张桦
（中国石油化工股份有限公司齐鲁分公司研究院，山东淄博255400）
关键词PVC;MBS；增韧增强；管件
Vol.41, No.6 Jun.,2013
[摘要］研究了冲击改性剂MBS的种类和用量以及刚性改性剂树脂A的用量对PVC一M管件性能的影响。结果表明：当B一x用量为15份.树脂A用量为10份时，PVC一M管件达到了刚韧平衡，性能达到了CJ/T272 2008给水用抗冲改性聚氯乙烯(PVC一M)管材及管件》的要求。
［[中图分类号］TQ325.3［文献标志码］B
3［文章编号］1009—7937(2013)06—0018—04
Rigid-toughness balance of PVC-M pipe fittings SUN Peipei,LI Jing,LIU Rongde,ZHANG Hud
(Research Institute of Qilu Branch Co ., SINOPEC,Zibo 255400,China)
Key words : PVC; MBS ; toughening ; reinforcing; fitting
Abstract: The effects of the kind and dosage of impact modifier MBS and the effects of the dosage of rigid modifier resin A on the properties of PVC pipe fittings were studied . The results showed that : the rigid-toughness balance of PVC pipe fittings was achieved when B-x dosage was 15 phr and resin A dosage was 1O phr . The properties of PVC pipe fittings met the requirements in CJ / o
高抗冲聚氯乙烯（PVC一M)管材很好地解决了 PVC管材韧性较差的间题，从而扩大了其应用领域，而与之相配套的PVC一M管件也迅速发展起来。与PVC一U管材、管件相比,PVC一M管材、管件的优点在于：①在保持弹性模量的同时，设计应力明显提高，管壁可减小30%：②韧性显著改善，冲击强度可达到PVC一U管材、管件的6～10倍：③可以容许一定程度的弯曲变形，提高了抗震性、抗地基不均勾沉降的能力、抗水锤和点载荷的能力以及管道运行的安全性，同时方便搬运、运输。
PVC一M管件要求具有高刚性、高韧性，普通 PVC材料很难达到此要求，需要进行大幅度的改性。对PVC进行抗冲改性常采用加入冲击改性剂的方法，常用的有氯化聚乙烯（CPE）、丙烯酸酯共聚
*［收稿日期］2013—05—10
物（ACR)、甲基丙烯酸甲酯一丁二烯一苯乙烯三元接枝共聚物（MBS）、丙烯晴一丁二烯一苯乙烯共聚物（ABS）、乙烯一乙酸乙烯酯共聚物（EVA)以及乙内橡胶（EPR)等。其中MBS树脂是一种高分子材料，一般采用乳液接枝聚合法制备，在亚微观形态上具有典型的核一壳结构，核心是一个直径为10～100 nm的橡胶相球状核，外部是苯乙烯和甲基丙烯酸甲酯组成的壳层。由于甲基丙烯酸甲酯与PVC的溶解度参数相近,在PVC树脂和橡胶粒子间起到界面粘接剂的作用,在与PVC加工混炼过程中形成均相；而橡胶相则以粒子状态分布于PVC连续介质中,呈现海岛结构，这种特殊结构赋予了PVC制品优异的冲击性能行。