第43卷第7期 2015年7月
聚氯乙烯 Polyvinyl Chloride
耐度PVC一M管材的性能及加工应用
李明顺”
（淄博职业学院化学工程系，山东淄博255314）
[关键调]PVC-M;耐磨改性；耐磨改性剂；碳酸钙晶须;玻璃微珠
Vol.43, No.7 Jul.，2015
[摘要】对用于PVC-M管材的耐率改性剂进行了筛选，研究了耐率改性剂对PVC-M管材性能的影响，并确定了耐磨改性剂用量；加工应用结果表明，必须对PVC~M管材配方进行些微调整才能适应不同加工设备的生产要求。
【中图分类号】TQ325.3，【文献标志码】B：
[文章编号］10097937(2015)07002305
Properties of abrasionresistantPVC-Mpipesand their processingand application
LI Mingshun
(Department of Chemical Engineering，Zibo Vocational Institute,Zibo 255314,China)
Key words: PVC-M; abrasion modification; abrasion modifier; calcium carbonate whisker; glass bead Abstract: The abrasion modifiers used in PVC-M pipes were selected. The effects of abrasion modi-
fiers on properties of PVC-M pipes were studied. The amount of abrasion modifier was determined. The results of processing and application showed that the formula of PVC-M pipes must be adjusted to meet the requirments of different processing equipment.
PVC管材具有摩擦阻力小、环刚度高、耐腐蚀性好、耐候性能好、性价比高以及维护成本低等特点，广泛应用于建筑排水、排污和化学工程等领域。但 PVC耐磨性较差，磨耗是致使材料破坏、使用寿命缩短的因素之一[1]。在输送含有废渣的液体时,PVC 管材因长时间与废渣接触摩擦而使壁厚变薄直至破损。目前国内有部分单位进行了耐磨PVC管材的研究。改善PVC管材的耐磨性能--般是选用质地较硬、结构不易被破坏且经过偶联处理的无机填料加人入到PVC中，如具有晶须结构的碳酸钙、硫酸钡等，但晶须材料比较脆，在加工中受到剪切等机械力的作用易被折断，导致PVC管材的耐磨性能提高有限。
笔者考察了耐磨改性剂的种类及用量对PVC-M管材耐磨性能的影响，并将得到的优化配方应用于实际加工，进一步考察其实用性。
1试验部分 1.1原材料
PVC树脂，QS-1050P，中国石油化工股份有【收稿日期】20150304
限公司齐鲁分公司氟碱厂；AS树脂（即SAN树脂），中国台湾奇美公司；MBS，日本进口：有机锡稳定剂、耐磨改性剂A、耐磨改性剂B、碳酸钙晶须、玻璃微珠均为市售。
耐磨改性剂A为硅的气相二氧化物；耐磨改性剂B为具有片状玉石结构的高硬度硅酸盐矿物质，来自于玉石加工的碎屑，通过研磨、筛选和偶联剂表面改性处理后，可增强与PVC分子的界面相容性，
从而大大提高PVC管材的耐磨性能。 1.2仪器及设备
SRL-Z型高低速混合机，张家港万塑机械有限公司；MZ-4602型耐磨测试仪，江苏明珠实验仪器有限公司；SK160B型双辊开炼机，上海橡胶机械厂；H-7000型扫描电子显微镜（SEM），日本日立公司：WDW-20型拉力机，上海华龙测试仪器有限公司：IDT537A型热模压机，日本安田精制会社;6545/000型冲击强度仪，意大利CEAST公司： 6951/000型切口机，意大利CEAST公司。
【作者简介】李明顺（1967一），男，副教授，工学硕士，1990年毕业于青岛化工学院高分子材料加工机械专业，现从事
教学工作。
23