煤矿用三层共挤PVC-M管材配方的开发
刘容德，，李静，张桦，刘浩
（中国石油化工股份有限公司齐鲁分公司研究院，山东渊博255400）
【关键词】PVC；管材；共挤；冲击性能；抗静电；煤矿
Vol.44,No.1 Jan.，2016
【摘要】通过对基础树脂、稳定体系、润滑体系、增韧体系的研究，确定了煤矿用三层共挤PVC-M管材中间层的配方；通过对导电性能、熔体流动性的研究，确定了煤矿用三层共挤PVC-M管材内外层的配方。产品的综合性能测试结果表明：研制的煤矿用三层共挤PVC-M管材具有良好的导电性能、较高的拉伸强度及冲击强度，达
到了技术指标要求。
【中图分类号］TQ325.3
【文献标志码】B【文章编号］10097937(2016)01-0023-05
Development of formula of three-layer co-extrudedPvC-M pipefor coal mines
LIU Rongde, LI Jing, ZHANG Hua, LIU Hao
(Research Institute of QiluBranch Co.，SINOPEC，Zibo 255400，China)
Key words: PVC; pipe; co-extrusion; impact property; antistatic; coal mine
Abstract: The formula of middle layer of three-layer co-extruded PVC-M pipe for coal mines was developed by studying base resin, stability system, lubricating system and toughening system. The formula of inner layer and outer layer of the three-layer co-extruded PVC-M pipe was developed by studying con-ductivity and melt flowability. The test results of comprehensive property showed that the prepared three-layer co-extruded PVC-M pipes for coal mines had good conductivity, higher tensile strength and impact strength, and met the technical requirements.
目前，PVC-M管材已经大量生产，广泛应用于城乡和建筑给水、矿山等。PVC-M管材的冲击性能优异，能很好地抵抗管材安装和运输过程中的外力冲击，防止快速开裂。然而，PVC-M管材在煤矿中应用时存在抗静电性能差的缺陷。国家煤炭部标准MT558.2一1996《煤矿用聚氟乙烯（硬）管材》规定了用于煤矿井下抽出瓦斯的PVC管材的表面电阻应小于1×10°。文献资料表明：采用在 PVC-M管材中添加抗静电剂的方法，管材的表面电阻通常在1×10°~1×10n[1-2)只有在PVC-M管材中添加6份左右的纳米超导电炭黑后才能达标。可是，这样做不但会使PVC-M管材的力学性能大幅下降，管材变脆，失去PVC-M管材冲击性能优异的优点，还也会对PVC-M管材的挤出加
，【收稿日期】20150322
工造成困难。
为解决上述间题，笔者对PVC-M管材的配方
进行了研究。 1试验部分 1.1主要原材料
PVC树脂，QS-1050P、QS-1000F、S-1000、 S-700，中国石油化工股份有限公司齐鲁分公司氯碱厂；ACR，401，淄博华星助剂有限公司；CPE， 135A，潍坊亚星化工有限公司；DOP，山东齐鲁增塑剂股份有限公司：MBS，日本进口：有机锡稳定剂、润滑剂，市售；轻质碳酸钙，常州碳酸钙有限公司；纳米导电炭黑，捷克进口。
【作者简介】刘容德（1968一），男，高级工程师，1989年毕业于青岛科技大学高分子材料系，现从事PVC树脂改性方
面的研究。