模具技术2017.No.4
文章编号：1001-4934(2017)04-0001-05
基于Moldflow和Taguchi方法的汽车长饰条
工艺参数优化
杨蒸燕，向良明，庄瑞英，黄龙辉
（泛亚汽车技术中心有限公司，上海201201）
1
摘要：运用Moldflow软件，结合Taguchi方法，分析在注塑过程中模具温度、熔体温度、保压压力、保压时间对汽车长饰条变形量的影响。通过四因素三水平的正交试验，得出模具温度为70℃、熔体温度为260℃、保压压力为注射压力的80%、保压时间为10s是最佳注射工艺参数。优化后翘曲变形量为1.214mm，比优化前降低了37
个百分点。经过试模，得到了高达93%以上的尺寸合格率。关键词：汽车长饰条；Moldflow；变形；注塑成型；Taguchi方法
中图分类号：TP391.7
文献标识码：B
The injection parameters optimization of auto deco trim based on Moldflow and Taguchi
YANG Yan-yan,XIANG Liang-ming,ZHUANG Rui-ying,HUANG Long-hui
Abstract: The simulation of injcction molding for the auto deco trim of automobile was per-formed based on analytical software Moldflow with Taguchi method.The effects of melt temperature, mould temperature, packing pressure and packing time on the warpage of the deco trim were analyzed. Using the orthogonal test of 4 factors/3 levels, the best process parameters are obtained as follows:mould temperature is 70C,melt temperature is 260C packing pressure is the 80% of injcction pressure, and the packing time is 10 s. After the optimization thc warpage is 1.214 mm, which is reduced by 37 percentage points. After mould trial, thc pass rate of part size can reach 93%
Keywords: auto deco trim; Moldflow, warpage; injection molding; Taguchi method
长期以来，工艺参数的设置都是凭借经验获取，
0引言
大量的汽车塑料零件通过注塑成型，其质量受模具设计、材料性能及成型工艺参数等多种因素的影响。其中成型工艺对模具中的熔体流动和最终制品质量有直接影响，因此注塑工艺参数优化一直是注塑设计人员关注的问题。
收稿日期：2017-02-14
作者简介：杨燕燕（1983一），女，工程师。万方数据
随着CAE技术的迅速发展，特别是Moldllow 软件的推出和运用，它模拟熔体的流动，为工艺参数的优化提供了仿真前提。
Taguchi方法是日本田口玄一博士创立的，是一种因素试验设计技术，主要基于一定的规则设计正交试验矩阵，确保以最小数目的试验次数获得影响性能参数的全部信息，找出所有