模具工业2017年第43卷第1期
指针小孔成形凸模与凹模用钢研究
李文平
（四川信息职业技术学院机电工程系，四川广元628040）
摘要：以成形指针的模具零件为研究对象，对用不同材料Cr12MoV钢和7Cr7Mo2V2Si钢制作的小孔凸、凹模的磨损量和刃磨寿命进行了研究。结果表明：用7Cr7Mo2V2Si钢的模具零件比Cr12MoV钢的正常
磨损阶段更长，模具零件的平均刃磨寿命可延长50%，具有明显的优越性，关键调：7Cr7Mo2V2Si钢；Cr12MoV钢；模具；磨损量；刃磨寿命；折断率；指针
中图分类号：TG76;TG142
文章编号：1001-2168(2017)01-0071-04
文献标识码：B
D0I:10.16787/j.cnki.10012168.dmi.2017.01.018
Research on steelforpunch and matrix forming
needlesmallhole
LI Wen-ping
(Department of Mechanical-and Electrical Engineering,Sichuan Vocational College of
Information Technology,Guangyuan,Sichuan628040,China)
Abstract: Taking the die parts for forming needle as research object, the wear extent and service life of the punch and matrix with different materials of Cr12MoV steel and 7Cr7Mo2V2Si steel were studied. The results showed that the service lifeof 7Cr7Mo2V2Si steel die parts was increased as much as 50% than Cr12MoV steel.
Key words: 7Cr7Mo2V2Si steel; Cr12MoV steel; die; wear extent; service life; broken rate; needle
引言 0
常用仪表的指针零件如图1所示，该零件上的孔径尺寸较小为d0.5mm，对冲孔的凸模及凹模有特殊要求。这类小孔冲模的损坏主要是磨损失效及小孔凸模折断。
20e
3
图1指针
成形指针的模具零件磨损失效部位主要存在于冲小孔凸、凹模刃口部位、凸模端面、凸模圆柱面以及凹模型孔表面。模具的冲裁过程：凸模与凹模组成上、下刃口，板料放在凹模上，凸模在压力机的
收稿日期：2016-10-25。
作者简介：李文平(1983-)，男(汉族)，四川巴中人，讲师，主要从
事模具设计与制造技术、职业技术教育等方面的研究。万方数据
71
滑块带动下下行，将板料压入凹模中，板料在经过弹、塑性变形后发生断裂分离。模具零件的磨损主要发生在冲裁过程中及冲裁结束阶段。凸模在将板料压入凹模的最初阶段，凸、凹模刃口部位受到拉压交替的应力，随着冲裁次数的增加，模具零件刃口处易出现疲劳裂纹，进而造成模具零件刃口磨损"-"。同时，凸模端面与板料接触面之间的摩擦也会造成凸模端面磨损。在继续将板料压入凹模的最终阶段，一般凸模伸进凹模深度为一个料厚t，随后凸模随压力机滑块上行脱离板料。但此时未被冲入凹模孔内的板料会紧紧套在凸模上，因为在冲裁时材料受到了凸模的挤压，发生了沿凸模径向向外的挤压弹性变形，冲裁一结束材料将回弹紧抱凸模。卸下板料则需卸料力，约占冲裁力的8%左右，在卸料过程中会造成凸模外圆柱面磨损。
随着模具使用次数增加，凸、凹模刃口磨损、端面磨损以及圆柱面的磨损都从微量磨损逐渐累积成过量磨损，最后导致凸、凹模间隙变大及刃口钝化。如果凸模尺寸小，强度本身不足，在刃口变钝