冷扩孔并置入栓钉技术止裂效果研究
Studyon Fatigue Repair with Stop Hole Techniques
黄鑫‘，沈玫1，郭阿明2
（1.中国中元国际工程公司，北京100089;2.中国中轻国际工程有限公司，北京100026）
HUANG Xin',SHEN Mei",GUOA-ming
(1.China IPPR IntemationalEngineeringCorporation,Bejing 100089,China; 2.China BCEL Intermational Engineering Co. Lid., Beijing 100026,China)
建策与结构设计
Amatrdndarnraber
【摘要】采用有限单元法对冷扩孔并置入检钉处理措施进行数值模拟，并对描环荷载下止裂孔孔边应力、应变状态的分析表明，冷扩孔并置入检行降低了应力集中部位的应变幅，从而延长减劳裂纹在止裂孔边的再生寿命，检钉直径均会影响钻孔止裂相关技术的止裂效果，
[Abstract ]To understand the mechanism of stop bole related techniqucs--inserting interference fit fastener are simulated numerically with finite element metbod, The analysis and comparison of the stress and strain around the stop hole under cyclic
loadingshowtbatinserting interference fit fastenertechniquesreduce thestrainrange toextendcrackre-initiation life.【关键词】普通止裂孔；冷扩孔并置入检钉；应变幅；裂纹再生寿命
[Keywords ]stophole;insertinginterferencefitfasteners;magnitudeofstrain;thelife offatiguecracking
【中图分类号】TU39 1概述
【文献标志码】A
自前钢结构广泛应用于桥案、机减、工业和公共建筑，险着钢结构的广泛应用，对其维护的重要性也显得越来越突出。疲劳是一种钢结构常见的破坏形式。钢结构的疲劳是指钢结构构件在循环应力、应变的反复作用下，形成裂纹而破坏的现象。当钢结构构件承受德环荷载作用时，可能由于疫劳而产生裂纹，疲劳裂纹的扩展将导致构件因脆性断裂而失效，这种损于疲劳的脏新往往在应力水平很低的情况下突然发生，无明显塑性变形，将造成极大的经济损失甚至人员伤亡。此外，恶劣的工作环境如低温、蚀及冲击荷载等将进一步削弱钢结构的疲劳性能。研究表明，与疲劳有关的胞断破坏是大鼠钢结
【作著简介】黄高（1982~），男，山东菜州人，工程师，从事结构工程设计与研究，（电子信箱）huangxin@ippr.net。
万方数据
[文章编号】1007-9467(2012)06-0068-03
构事故的主要原因间，因此在钢结构的日常维护中一且发现疲劳裂纹，应及时更换开裂构件。而由于费用、工期等原因无法更换开裂构件时，应立即对可能起断裂的疲劳裂纹进行止裂和修复，延长钢结构构件的疲劳寿命，避免脆断事故的发生。止裂与修复处理的时机和方法应根据疲劳寿命预刻及钢构件的受力和开裂情况确定，过度的或不恰当的止裂与修复处理将不但增加钢结构维护的费用，而且可能恶化钢构件的疲劳性能，加速脆断的发生。因此，探索有效、可靠的疲劳裂纹止裂与修复方法是安全、经济地处理钢结构疲劳、断裂问题的关键，具有重大的社会意义和广阔的应用前景。
钻孔止裂技术是贯通型疲劳裂纹最常用的临时修复技术之一。它不仅适用于钢结构构件，而且适用于机械零部件等其它金属构件。
钻孔止裂通常是在裂纹尖端钻一确定直径的光滑圆孔，如图1所示，其止裂原理在于消除裂纹尖端的应力集中，阻止
67