2.25Cr1Mo0.25V钢焊接材料再热裂纹敏感性评估
李秀杰，段莉蕾，谷文
（中国第一重型机械集团大连加氢反应器制造有限公司，辽宁大连116113）
摘要：针对2.25Cr1Mo0.25V钢加氢反应器产品的焊接再热裂纹敏感性，按照API934#A附录B(2012）推荐的试验方法对 2.25Cr1Mo0.25V埋弧焊焊丝/焊剂开展再热裂纹试验，以便评估该焊接材料再热裂纹的敏感程度，
关键词：再热裂纹；埋弧焊；敏感性中图分类号：TG457.11
SAWweld metal evaluation of sensitivity of reheat cracking
of2.25Cr1Mo0.25Vsteel Li Xiujie,Duan Lilei,GuWen
(CFHI Dalian Hydrogenation Reactor Co. , Lid., Dalian 116113,Liaoning,China)
Abstract: In order to evaluate the sensitivity of hydrogen reactor, produced by CFHI and made of 2. 25Cr -1Mo 0.25V steel, to the reheat crack, the reheat cracking sensitivity of 2.25Cr 1Mo 0.25V SAW welding wire / flux which were produced by the Japanese Kobe Steel was tested according to the test method recommen-
ded by the 934 A B (2012). Finally, the sensitivity of this materials was evaluated. Key words: reheat cracking; SAW; sensitivity
0前言
2008年初，欧洲25台2.25Cr1Mo0.25V钢厚壁加氢反应器遇到了焊缝金属再热裂纹问题"。各地方实验室做了大量的研究调查，通过Gleeble高温拉伸试验对焊接材料再热裂纹的敏感性进行了等级划分，作为焊接材料筛选试验[2-3]，避免今后的焊缝在后续的热处理过程中产生再热裂纹。
但是Gleeble拉伸试验设备作为实验室的非常规设备，在大多数实验室不具备可行性。于是优化了这种试验，利用常规拉伸试验机进行再热裂纹敏感性筛选试验，并于2012年将这种试验方法纳人到了API 934A附录B(2012)中(4-6)。
中国一重在2001年首次制造了第一台设计温度 454℃，质量540t的钒改进钢锻焊加氢反应器(7)。目万方数据
前为止已经生产了多台2.25Cr1Mo0.25V钢加氢反应器，还未发现在低合金钢焊缝中存在再热裂纹问题。早在2011年，中国一重已经采用多种方法进行了加钒钢焊接材料的再热裂纹试验。从2013年开始，中国一重承揽的一些加氢反应器产品技术条件中增加了对 2.25Cr1Mo0.25V钢焊接材料进行再热裂纹检测的要求[8-9]。为了满足技术条件要求，对2.25CrlMo0.25V 钢配套的日本神钢公司生产的埋弧焊焊材按照API934-A附录B要求进行再热裂纹敏感性筛选试验，以验证焊缝的再热裂纹敏感性。
试验材料及方法
按照API一934附录B要求的试验程序如下。
1.1试板焊接 1.1.1母材