5083铝合金焊接接头腐蚀性能及力学性能损失分析
路全彬，龙伟民，沈元勋，杜全斌，孙华为
（郑州机械研究所新型针焊材料与技术国家重点实验室，河南郑州450001）
摘要：采用浸泡试验和失重法研究了5083铝合金焊接接头腐蚀行为，并对接头进行室温拉伸测试，通过扫描电镜对接头进行微观形貌分析和断口分析。结果表明，5083铝合金焊接接头不同区域腐蚀性能存在显著差异。焊缝区耐腐蚀能力最差，热影响区次之，母材最耐腐蚀。焊缝区成分、组织不均、并存在残余应力，造成此区耐腐蚀性最差。焊接接头经过腐蚀后，断裂方式发生改变，接头强度损失严重。
关键调：铝合金；焊接接头：耐腐蚀性能；力学性能中图分类号：TG457.14
The corrosion resistance and mechanical properties of welding
jointof5083aluminiumalloy
Lu Quanbin, Long Weimin, Shen yuanxun, Du Quanbin, Sun Huawei
(Zhengzhou Research Institute of Mechanical Engineering, State Key Laboratory of Advanced
Brazing Filler Metals and Technology,Zhengzhou 450001, China)
Abstract: Immersion test and weightlessness were used to study the corrosion behavior of 5083 aluminium alloy welding joints, The corrosion microstructure and fracture were analyzed by scanning electron microscopy. The re sults show that corrosion behavior of 5083 aluminium alloy welding joints were difference among the weld zone, the heat affected zone and the base metal. The weld zone corrosion resistance is the worst, followed by the heal affected zone, thus the base metal is most corrosion resistance. The weld zone corrosion resistance is the worst because of heterogeneous microstructure and residual stress. The strength of the welding joints loses heavey after corrosion.
Key words: aluminium alloy; welding joint; corrosion resistance; mechanical properties
0前言
铝和铝合金焊接已经广泛应用于高速列车、地铁、轻轨等城市轨道交通，军工领域，汽车车辆和船舶、储罐行业等，并且对焊接质量要求较苛刻1)。铝合金焊接接头存在化学成分、组织和力学性能的不均，焊接变形和残余应力的存在，对接头腐蚀性能造成很大影响[2-4]。焊接接头的腐蚀对整个焊接构件的可靠性造
成很大的影响(5)。万方数据
报道中，关于铝合金在腐蚀条件下的强度性能已进行大量研究，如Alexoppoulos等人(6)研究了预腐蚀对铝合金拉伸性能和断裂韧性的影响。Bums等人[研究了腐蚀对铝合金疲劳极限的影响。但关于铝合金焊接接头腐蚀与强度的损失研究相对较少。
文中首先研究了5083铝合金焊接接头在酸性腐蚀溶液中的腐蚀行为，取得铝合金焊接接头试样的腐蚀性能数据，然后对接头进行力学性能测试，评价腐蚀行为对力学性能损失的影响。
2016年第1期9