河北冶金 HEBEIMETALLURGY
抗震钢筋的性能优化
间忠峰
（河钢集团宜钢公司一钢轧厂，河北宣化075100）
Total No. 256 2017,Number4
摘要：分析了宣钢一钢轧厂生产的HRB400E抗震钢筋力学性能不稳定因素，采取修订化学成分执行标准、优化转炉工艺操作等措施后，钢筋的性能控制水平显著提升，综合窄成分命中率提高4.2%，屈服强度均值提高18MPa，极差由优化前的77MPa降至54MPa，分布离散性收窄，实现产品零质量异议目标。关键词：抗震钢筋；性能；优化
中图分类号：TG335.6
文献标识码：B
doi : 10. 13630/j. cnki. 13 1172. 2017. 0414
文章编号：10065008（2017)04005203
PERFORMANCEOPTIMIZATION OFASEISMICREINFORCEMENT
Yan Zhongfeng
( No. 1 Steel Rolling Mill, HBIS Group Xuansteel Company, Xuanhua, Hebei, 075100 )
oeaeeaaoee ance control level of the steel bar is improved significantly after adopting the measures of revising standards for the chemical composition and optimizing the converter operation. The narrow component hit rate is in-creased by 4. 2% , mean yield strength is increased by 18 MPa, and the range is reduced from 77 MPa to 54
MPa. The distributing dispersion is narrower and achieve the goal of zero quality demurral. Key Words: aseismic reinforcement, performance, optimization
引言
近些年频发的地震，对建筑用钢筋的强度、韧
性、焊接性提出更高的要求，在这一背景下抗震钢筋应运而生，其最大的优点是抗拉强度和延伸率都比较大，抗震能力提高，倾斜时不易发生断裂，减少伤亡。表征抗震钢筋质量的重要标志是：性能符合标准、表面质量良好、外观尺寸控制精度符合标准，性能指标主要有屈服强度、抗拉强度、强屈比和屈标比等，稳定的强度指标主要体现在的钢中化学成分的控制。所以，优化化学成分、提高窄成分达标率成为炼钢环节保证抗震钢筋力学性能的重要途径。
生产工艺概况
1
宣钢一钢轧厂产品主要有建筑用钢筋、电力铁塔用角钢、低碳带钢、焊条钢等，其中建筑用三级、四级抗震钢筋是主要冶炼钢种，产量约占65%：产品
收稿日期：2017-01-13
作者简介：闫忠峰（1969－），男，硕士研究生，高级工程师，2013年毕业于北京科技大学冶金工程专业，现在河钢集团宣钢公司一钢轧厂从事炼钢技术研究工作，E-mail:yanzf69@163.com
52
万方数据
系列化可为用户提供Φ16~32mm直条和Φ8~ 12mm盘条不同规格的带肋钢筋。
生产工艺流程
1.1
高炉铁水一转炉钢水一氩站处理一连铸铸坏加热炉加热一高压水除鳞一粗轧一中轧一精轧成材 1.2技术条件
以三级抗震钢筋为例.其性能要求如表1所示不同规格的钢筋对应不同的化学成分，确保钢筋的力学性能稳定。
表1HRB400E钢筋的性能要求
Tab. 1 Performance requirement of HRB400E rebar
届服强度
抗拉强度
(Rel)/MPa
(Rm)/MPa
≥430
2
560
强屈比(Rm/Rel) 31.25
性能不稳定的原因
现状
2.1
屈标比 ≤1.30
断后伸长率/% 9
2015年我厂生产的钢材发生质量异议共有18 次，其中抗震钢筋异议占27.8%。对问题批次钢筋取样分析，全部为强度低于标准或处于边缘（表2）。