0
总第255期 2017年第3期
河北冶金 I METALLURGY
HEBEL
宣钢SWRH82B盘条控冷工艺的研究
孙先焦
（河钢集团宣钢公司技术中心，河北宣化075100）
Total No.255 2017,Number3
摘要：利用Gleeble热模拟试验机对宣钢SWRH82B盘条的CCT曲线进行测量绘制，采用金相法进行验证.研究了冷却速度对SWRH82B组织相变的影响。结合宣钢设备现状，确定适用于宣钢Φ12.5mm
规格的SWRH82B盘条生产的控冷工艺为相变前冷速控制为7~10℃/s为宜。关键调：SWRH82B盘条；CCT曲线；冷却速度；金相组织；控冷工艺
中图分类号：TG335.6
文献标识码：A
doi;10. 13630/j. cnki. 13 1172.2017.0305
文章编号：10065008(2017)03002404
RESEARCHABOUTCONTROLLEDCOOLING
PROCESSOFSWRH82BWIREBARINXUANSTEEL
Sun Xianjiao
(Technique Center, Hesteel Group Xuansteel Company, Xuanhua, Hebei, 075100)
Abstract: The CCT curve of wire bar SWRH82B is measured and drawn with Gleeble hot modeling test machine, and confirmed with metallographic method, the influence of cooling speed on the structure phase transformation of SWRH82B studied.Based on the present situation of equipments in Xuan Steel,the controlled cooling process for wire bar SWRH82B of p 12.5 mm is determined as 7 to 10 C/s for cooling speed before phase transformation.
Key Words: wire bar SWRH82B; CCT curve; cooling speed; metallographic structure; controlled cooling process
引言
SWRH82B盘条主要用于制作高品质预应力钢
丝、钢绞线，是我国发展速度较快的一种经济高效建筑钢材。随着现代制造技术、自动化控制技术的快速发展，线材深加工拉拔速度已由原来2.5m/s提高到8.0m/s，必然要求SWRH82B盘条具有较高的索氏体比例和均匀的金相组织"]，同时不得出现二级以上的网状渗碳体和马氏体组织，因此要有合理的冷却工艺进行控制。CCT曲线反映了在连续冷却条件下过冷奥氏体的转变规律，是制定合理的控冷工艺、得到适宜的金相组织的理论依据[2]。因此，研究SWRH82B盘条的CCT曲线及其相变规律，对制定合理的控冷工艺具有重要的指导意义。
收稿日期：2017-01-03
作者简介：孙先焦（1987-），男，工程师，2009年毕业于武汉科技大学金属材料工程专业，现在河钢集团宣钢公司技术中心从事产品研
发工作，E-mail;xgsunxj@163.com 24
万方数据
1 1.1
试验材料、试样尺寸试验材料
试验所用材料为宜钢生产的SWRH82B盘条，
其化学成分见表1。
表1SWRH82B的化学成分 Tab.1
Chemical composition of SWRH82B
c 0.82
1.2
si 0.24
试样尺寸
Mn 0.77
P 0.012
s 0.005
% $
0.22
热模拟试验试样取材于宣钢@12.5mm规格
SWRH82B盘条，通过线切割加工成Φ4.0mm×10 mm圆棒试样，如图1所示。