宣钢ER70S-6盘条拉拨断裂原因分析
沈俊杰
（河钢集团宜钢公司技术中心，河北宣化075100）
Total No. 259 2017,Number7
摘要：针对宣钢ER70S-6盘条在拉拨至Φ0.8~1.2mm时发生断裂间题，对断口进行了宏观形貌、化学成分、夹杂物及显微组织的分析。结果显示，盘条心部形成的马氏体组织经强烈变形后产生严重的加
工硬化是导致拉拔断裂的主要原因。同时提出了相应的盘条生产工艺的控制措施。关键词：ER70S-6盘条；杯锥状断口；马氏体组织
中图分类号：TG142.1
文献标识码：A
doi :10. 13630/j. cnki. 13 1172.2017.0703
文章编号：10065008（2017)07001003
DRAWINGFRACTURECAUSEANALYSIS OFER7OS-6WIRERODOFXUANSTEEL
Shen Junjie
(Technology Center,HBIS Group Xuansteel Compamy，Xuanhua,Hebei, 075100）
Abstract: The fracture of ER70S 6 wire rod occurred at drawing to 0. 8 ~ 1. 2 mm. The macrophoto chemical composition,inclusion and microstructure of the fracture were examined, and the results showed that the serious work hardening of the martensite structur formed at the center of the wire rod occured after severe deformation, which was the main cause of the drawing fracture. At the same time, the corresponding control measures of wire rod production were put forward.
Key Words : ER7S 6 wire rod; cup cone fracture; martensite structure 引言
ER70S-6是气体保护焊丝主要牌号之一，该牌
号焊丝成本低，在焊接时具有较好的电弧稳定性和较高的焊缝性能，在国内外得到普遍使用。近期，宣钢生产的Φ5.5mm规格ER70S-6盘条供某客户拉拨使用时发生了断裂，断裂均发生在二次拉拨或桶装缠绕工序，断裂直径为Φ0.8~1.2mm，给用户带来较大的损失。为此对拉拨断裂试样进行分析，以期找到拉拨断裂原因，并提出盘条生产工艺的改进措施。
1
断裂形貌分析
Φ5.5mm规格ER70S-6盘条拉拨至Φ0.8
~1.2mm直径钢丝时发生断裂断口为杯锥状，其
断口形貌如图1所示。收稿日期：2017-04-16
作者简介：沈俊杰（1964-），男，高级工程师，1986年毕业于唐山工程技术学院轧钢专业，现在河钢集团宜钢公司技术中心从事工艺技术管理和新产品销售工作，Email:LiuzL.123@163.com
10
万方数据
图1断丝样品形貌
Fig. 1 Sample appearance of broken wire
断口呈杯锥状，一端为杯底，周围高高的杯壁，另一端成尖锥状。锥顶处断裂方式为脆性断裂；锥身为韧性断裂；锥底为脆性断口，并且锥底与锥身交界处存在明显的裂纹。同时对ER70S-6盘条拉拨断裂试样任何位置施加压力都可造成该种杯锥状