总第261期 2017年第9期
河北治金 HEBEIMETALLURGY
95CrMo钢穿管异常分析与改进
李双居"，王兵”，杭亮'，孙玉春'，赵瑞华
Total No. 261 2017,Number9
（1.河钢集团石钢公司，河北石家庄050031；2.河北工业职业技术学院汽车工程系，河北石家庄(1600S0
摘要：通过对管坏缺陷位置成分、高倍分析，结合对应炉次圆钢的高倍、组织分析，最终确定由于圆钢存在较严重的碳化物偏析，在加热、穿管过程中产生过烧，导致轧件产生分层、粘连芯棒、爆管事故。将穿
管加热温度由1090℃降低至1030℃后，消除了爆管事故，保证了正常生产。关键调：95CrMo钢；粘连；偏析；过烧；分析；改进
中图分类号：TG142.1
文献标识码：A
doi;10. 13630/j. cnki. 13 1172.2017.0908
文章编号：10065008(2017)09002703
ANALYSISANDIMPROVEMENTOF
ABNORMALTUBEFORMINGOF95CRMOSTEEL Li Shuangju', Wang Bing’, Hang Liang', Sun Yuchun', Zhao Ruihua
(1. HBIS Group Shisteel Company, Shijiazhuang, Hebei, 050031; 2. Automotive Engineering Department, Hebei Vocational and Technical College, Shijiazhuang , Hebei 050091)
Abstract: The cause of abnormal piercing was determined through the composition and high magnification morphology analysis of the defect position of tube billet, and the microstructure analysis of the round steel with the corresponding batch number. The reason is as follow: there is serious carbide segregation in the round steel microstructure which will cause the over burning during heating and piercing, It and that leads to delamination of rolled piece, adhesion of mandril and tube burst. The tube burst can be avoided through reducing the heating temperature from 1 090 C to 1 030 C during tube forming process. The production returns to normal.
Key Words: 95CrMo steel; adhesion; segregation; over burning; analysis; improving
0
引言
作为钎具钢的代表钢种95CrMo钢因具有抗疲
劳、抗震动性能较好，缺口敏感性低等一系列的优良性能，深受中空钎杆生产厂家的青睐。某公司采用 Φ60mm规格的95CrMo圆钢生产中空钎杆，某炉号95CrMo圆钢钢材穿管后减径轧制过程中发生芯棒粘连事故，无法正常生产、但其他炉号钢材无此现象，均可正常使用。本文通过对缺陷样品进行高倍分析，对圆钢进行高倍、组织分析，找出了产生异常
的原因并提出了相应的改进措施。收稿日期：2017-06-06
作者简介：李双居（1982－），男，工程师，2006年毕业于河北理工大学金属材料工程专业，现在河钢集团石钢公司技术中心从事产品开
发工作,Email:sglishuangju@ hbisco.com 万方数据
1
缺陷试样分析
用户生产中空钎杆的工艺：圆钢锯切下料（1
m）—中频加热（1090℃）一穿管带芯棒减径轧制一无芯棒减径轧制一拉拔成六方型钎杆。某炉次钢材在穿管后带芯棒减径轧制过程中产生钢材与芯棒粘连事故，无法正常生产。在芯棒与钢材粘连严重的位置及目视表面无明显异常的位置分别取样进行分析，缺陷试样宏观形貌如图1所示。图1中试样A为芯棒与钢材粘连严重位置的试样，试样B为目视表面无明显异常位置的试样，试样B外表面无异常但内表面已经出现粘连。
27