42CrMo曲柄异常组织分析和改善
AnalysisandImprovingofAbnormal Microstructurein42CrMoCrank
王继良
（中国核工业第五建设有限公司，上海201512）
WANGJi-liang
(China Nuclear Industry Fifth Construction Co. Ltd., Shanghai 201512, China)
工程施工技术 Cauoructicn Teckinala
【摘要1对调质后的42CrMo曲析进行了金相和扫描组织分析，结果显示：组织中存在大量块状白亮异常组织和极少量纯铁素体组织，白组织显微硬度偏低，碳化物密度较小，实质上是没有泽逹的上贝民体组织，纯铁素体组织是图火过程中的等温产物，对油槽进行加深和增加搅拌改造后，萍火冷却能力提高，显著消除了异常组织，
[Abstract ]Microstructures after quenched and tempered of42CrMo crank wereMetallrugical and SEM analyzed. Results show that: there areamass ofwhite abnormal structuareand littleferritein thecrank.Mirco-hardness ofwhitestructure, with relativelylittle content carbidein it,is low,contrast to thematrix,infact, this structureisupperbainite whichproduced afterquenching withalowcoolingrate Ferrite is a kind ofisothermaled product during tempering. Cooling ability is improved after deepening the oil tank and installing the
stirring device, so the abnormal structureisremoved significantly【关键词】42CrMo;调质；贝民体；碳化物
[Keywords ]42CrMo; temper; bainite; carbide
【中图分类号】TG156.3
【文献标志码】A
[DOI]10.13616/j.cnki.gcjsysj.2017.11.060
1引言
[文章编号】1007-9467(2017)11-0193-03
感应痒火，表面硬化。在曲柄最大直径处取样，在金相下发现
42CrMo钢具有较高的强度和韧性，通常将调质后表面率火作为热处理方案。42CrMo调质后由于具有较高的疲劳极限和抗多次冲击能力，低温冲击韧性优良，被广泛用于发动机曲轴制造(.。42CrMo热处理后的组织类型较多，如果冷却过程没有率透，组织均匀性差，最终导致回火索氏体级别的恶化。本文分析了一种42CrMo曲柄的异常组织及产生原因，并
通过改造现有装备提高了产品的质量。 2试验材料与方法
曲柄采用42CrMo圆钢批量锻造成形空冷后，经连续式网带炉860℃加热90min，油冷6min，670℃回火120min，然后【作者简介】王继良(1974~），男，山东阳谷人，高级工程师，从事工
程材料分析与研究。万方数据
有大量白色异常组织，在扫描电镜下进一步放大观察。并比较正常和异常组织处的显微硬度，曲柄的材料成分经光谱检测，符合标准，如表1所示。
表142CrMo钢成分（质量分数）
成分 IS Mn s Mo
标准范围% 0.38~0.45 0.17~0.37 0.50~0.80 ≤0.035 ≤0.035 0.90~1.20 0.15~0.25
3试验结果与分析
3.142CrMo组织和硬度分析
实测值%
0.42 022 0.64 0.010 1100 1.08 0.16
调质后的试样经抛光和硝酸酒精腐蚀后，金相组织如图1 所示。可看出组织由回火索氏体基体和大量白块组织组成，白块内部带有密度较少的颗粒物，因此白块状物质不是纯铁素
193