总第207期 2015年12月
文章编号：10099700(2015)06003004
南方金属 SOUTHERN METALS
Sum.207 December2015
冷墩钢线材冷顶锻开裂问题分析及改善措施
刘春林，农之江2，张志明”
（1.北京科技大学冶金与生态工程学院，北京100083；2.宝钢集团广东韶关钢铁有限公司，广东韶关512100）摘要：冷镦钢是用来加工紧固件的钢铁材料.紧固件加工过程最容易出现的质量间题是锻头开裂，墩头开裂主要原因是线材的缺陷.文章结合实践经验，对冷缴钢线材冷顶锻开裂和产生此类质量缺陷的原因进行分析，并采取相应的改进，使项锻开裂得以改善。
关键词：冷敏钢；顶锻开裂；表面质量；夹杂；组织
中图分类号：TG142.41
文献标识码：B
Analysison&ImprovementMeasuresofColdForging
CrackingofColdHeadingSteelWire
LIU Chun-lin', NONG Zhi-jiang’ , ZHANG Zhi-ming
(1. College of metallurgical and ecological engineering, University of Science and Technology Beijing, Beijing 100083, P. R. China; 2. Baosteel Group Guangdong Shaoguan Iron and Steel Co. Ltd. ,Shaoguan Guangdong, 512123, P. R. China
Abstract: Cold heading steel is the steel materials for processing fastening pieces, The common quality problems of pro-cessing the fastening pieces are prone to cold forging cracking which was mainly caused by the heredity of wire defects. The problems of cold forging cracking of cold heading steel wire and the causes are stated, the countermeasures and methods for reducing the cracking are given, which help reduce the defect rate.
Key words: cold heading steel; forging cracking; surface quality; inclusions; organization
0前言
冷镦钢是用来加工紧固件的钢铁材料.紧固件是作紧固连接用的基础性零配件，应用极为广泛，被形象地称为“工业之米”.紧固件分为标准件紧固件和专用紧固件.紧固件加工流程：钢材表面酸洗处理 →涂层（石灰水）一→磷化一→冷拔→（球化退火处理） →+精拔→冷镦成型→搓丝→+（后部处理）（渗碳、油淬、回火、镀锌、喷油等).冷锻钢盘条加工的特点是：冷锻件变形量大（60%~80%），所承受的变形速度高.因此，对盘条的表面质量、内在质量、成分的均匀性、通条性能的稳定性、冷加工性能及尺寸精度均有很高的要求.冷镦钢除了保证必要的机械性能外，
最重要的是要保证其工艺性能收稿日期：2015-07-13
紧固件加工过程常见的质量问题是镦头开裂，镦头开裂的紧固件意味着产品报废，不能使用.因此，降低冷锻钢开裂率成为钢厂和紧固件加工企业最重要的研究课题.镦头开裂少了，意味着加工的紧固件产品合格率提高了，用户对钢厂的钢材产品质量满意，钢厂的钢材竞争力也提高了，
1冷镦钢冷顶锻开裂问题及技术研究现状
冷顶锻开裂是冷锻钢产品的共性质量问题，世界上做得最好的企业是日本神户制钢，开裂率约 0.7%.其次是台湾中钢的0.9%~1.0%，宝钢和浦项制铁约1%
国内其他钢厂生产冷锻钢盘条都遇到锻头开裂
作者简介：刘春林(1970－)，男，1994年毕业于东北大学金属压力加工专业，高级工程师，北京科技大学冶金工程专业硕士研究生，