总茅261期 2017年第9期
河北冶金 HEBEI METALLURGY
影响ML08A1钢冷顶锻开裂的原因分析
Toul No.261 2017,Number9
陈建东"，刘玉君？
600 苏张家港215625）
摘要：从生产工艺上分析了影响ML08AI钢冷项锻开裂的原因。分析结果认为：［A1]s低，[N]含量高，[A1]s/[N]小于6.0的比例大，且冷墩前氮的时效硬化危害没有得到有效消除；保护渣卷人铸坏、钙处理效果不好等多方面因素导致了ML08AI钢冷锻开裂。
关键调：ML08AI钢；冷顶锻开裂；原因
中图分类号：TG142.1
文献标识码：B
doi;10. 13630/j. cnki. 13 1172.2017. 0915
文章编号：10065008(2017)09005706
ANALYSISOFTHE
ECAUSEOFCOLDFORGING
CRACKINGOFSTEELMLO8ALINCOLDHEADINGUPSETTING
Chen Jiandong', Liu Yujun
(1. Technology Research Center, Hebei Jingye Group Iron & Steel Co. , Ltd. , Pingshan, Heibei, 050409 ; 2. Converter Steel making Plant, Jiangsu Shasteel Group Co. , Lid. Zhangjiagang,Jiangsu, 215625)
Abstract: The causes of cold heading upsetting cracking of ML08Al steel were analyzed from the production process. The resuit showed that many factors leaded to cold heading upsetting cracking of ML08Al steel, including the lower [ A1]s, the higher content of Nitrogen, the larger proportion of [ Al]s/N ≤6, the failure of effective elimination of aging hardening hazards of nitrogen before cold forging, mold powder entrapment in casling blank, poor effect of Calcium treatment.
Key Words; ML08Al steel; cold heading upsetting cracking; cause
0
引言
ML08A1钢可用于生产低级别的紧固件，如螺
栓、螺钉、螺母、销钉等，市场容量较大。其冷顶锻变形量1/3~1/411，成型速度超过100只/min。因此，除轧材必须要有良好的表面质量外，还需要对 ML08A1铸坏的化学成分、钢水氮含量进行有效地控制，确保ML08AI钢具有高的韧性、低的抗拉强度、氮的时效硬化危害小、大的断面收缩率和伸长
表1
Tab.1
项目国标要求内控要求
0.05 ~0.10 0.05 ~0.08
si 40.10 0.05
率，以满足大变形量的加工需要。
工艺流程
河北敬业钢铁集团有限公司ML08A1钢生产工艺流程：铁水KR预处理→150tLD→150tLF→R9 mcc（10机10流165mm×165mm）→热送加热炉 →高速线材轧机→成品检验入库。ML08AI钢的化学成分见表1。
ML08AI钢的化学成分
Chemical composition of ML08 Al
Mn 0.30 ~ 0.60 0.30 ~0.40
收稿日期；201706-06
作者简介：陈建东（1967-），男，工程师，1989年毕业于华东冶金学院钢铁冶金专业，现在河北数业钢铁有限公司技术研发中心从事纯
净钢的冶炼技术研究，Email;chenjiandong0731@126.com 万方数据
P 0.035 ≤0.025
≤0.035 ≤0.010
Al
wt% wt%
≥0.020 0.030 ~0.045
57