第31卷第3期 2010年6月
热处理技术与装备
RECHULIJISHUYUZHUANCBEI
热镀锌工艺及连续退火炉的相关设备
李熠，陈光宇
（哈尔滨松江电炉厂有限贵任公司黑龙江哈尔滨150078）
Vol.31,No.3 June2010
·工艺研究·
摘要：随着工业的发展，对于钢板的热镀锌的需求越来越大，对热镀锌的工艺水平也提出了更高的要求，因此近年来热镀锌钢板的连续退火技术发展变化很大。本文介绍了热镀锌工艺及对热镀锌产
生影响的相关因素，并对热镀锌钢板的连续退火炉的相关设备进行了介绍。关键词：热镀锌；连续火炉；工艺
中图分类号：TC174.443文献标识码：B文章编号：1673-4971(2010)03-0045-03
ReleventEquipments ofHot Galvanization Technology
and Continuous Annealing Furnace
LIYi,CHEN Guang-yu
(Harbin Songjiang Electric Fumace Factory Co.，Ltd.，Harbin Heilongjiang 150078,China)
Abstract: With the industial development, the growing demand for steel plate, the hot galvanizing process is required on a higher level. So the continuous annealing technology of the hot galvanizing steel plate vary widely in recent years, This article reveals hot galvanizing technology and relevent factors which affect the hot galvanizing. Furthermore, the relevent equipments of the continuous annealing furnace of the hot galva-nizing steel plate,are introduced.
Key words: hot galvanization; continuous annealing fumace;technology
1热镀锌连续退火技术发展简析
随着我国工业生产水平的不断发展，对于钢板防腐的需求不断提高，使钢板防腐这个问题在国民经济中具有越来越重要的经济意义，金属镀层防腐的方法因其原材料来源充足，生产成本低，得到了广泛的应用。目前常用的金属镀层方法有热镀法和电镀法。
镀锌板主要用于户外，其腐蚀环境比较恶劣，所以要求较厚的镀层。此外，镀层属于阳极保护，镀层不太均匀也间题不大，镀层越厚使用寿命越长，热镀锌的特点正好可以满足这些要求。电镀锌镀层均匀，与钢基结合牢固，并且表面缺陷也少，但是镀层
收稿日期：201004=04
厚度较薄，仅为热镀锌层厚度的五分之一到七分之一，且生产成本较高，产量也低，故目前热镀锌仍是钢板镀金属的较好及较常见的方法。
连续热镀锌技术是上世纪30年代由波兰人森吉米尔发明的。其工艺特点是采用直火加热方式使钢板表面强氧化，同时烧掉轨制油，然后在分开设置的加热段中采用辐射管加热方式在强还原气氛中长时间加热、均热，使带钢表面氧化膜还原而消除，在产生活化的带钢表面进行镀锌。
2带钢连续热镀锌工艺分析及影响镀层的主要因素
热处理工艺一般包括加热、保温、冷却三个过
作者简介：李烟（1978-），男，助理工程师，主要从事工业电炉热处理技术设计研究。
联系电话：13613651949;Emeil：alanin2009@163.com