铝合金三价铬钝化液的研制和应用
熊鹰，彭敬东？
（1.重庆长江造型材料集团有限公司，重庆400715；2.西南大学化学化工学院，重庆400715）
摘要：分析了铝合金三价铬钝化液的钝化机制，研究了复合盐钝化剂用量、钝化处理时间和温度对钝化膜质量的影响，结果表明，经铝合金三价铬钝化液钝化后的试样，其抗腐蚀性能优于铬酸钝化液，可在常温下进行处理，且处理时间较短，有利于减轻铬酸钝化液中六价铬离子对环境的影响。
关键词：铝合金；表面钝化；三价铬钝化液
中图分类号：TG174.4
文献标识码：A
文章编号：1673-3320（2010）05-00014-02
DevelopmentandApplicationofTrivalentChromiumPassivator
forAluminumAlloy Xiong Ying', Peng Jingdong?
(1. Chongqing Changjiang Moulding Material Group Co., Ltd., Chongqing 400715, China;
2. School of Chemistry and Chemical Engineering, Southwest University, Chongqing 40o0715, China) Abstract: The passivation mechanism of trivalent chromium passivator for aluminum alloy has beenstudied,includingadditiveamountofcomplexsaltpassivator,influenceof processingtimeand temperature on the quality of passive film.The test has shown that the samples treated by trivalent chromium passivator has improved anti-corrosion property. The treat process is at room temperature and
quite short.The impact on environment can be reduced without hexavalent chromium acid. Keywords:aluminumalloy;passivation;trivalentchromiumpassivator
铝在全球的产量仅次于铁。铝及铝合金具有诸多优点，如比强度高、导热和导电性好、反光性强、色泽美观、无磁性、耐蚀性和成形性好等等。因此铝及其合金在汽车、摩托车、飞机和船舶等工业中得到广泛应用。
铝及其合金在大气环境中会自动形成一层极薄的天然氧化膜，厚度仅为0.4～0.5nm。这层氧化膜结构不紧密、多空隙、无光泽、强度低、抗腐蚀能力较弱，因此对其表面进行涂装防护是必须的工艺。有机涂膜都是半渗透性物质，腐蚀性物质仍可不同程度地渗透进去，特别是在铝基材表面无化学转化膜的条件下，腐蚀性物质的渗入很快会使基材腐蚀。这种腐蚀主要是电化学腐蚀，阴极区的pH 值可以超过12.5，而阳极区的pH值可以降到1，在这种情况下，铝基体及自然氧化膜都开始溶解。正
因如此，有机涂膜下的铝合金基体一经腐蚀，涂膜与基体间结合力的丧失就远超过钢铁件。
提高有机膜结合力，降低涂膜下基体腐蚀的
主要措施是使其表面生成一种能耐pH变化的转化膜。用作涂装的转化膜主要有：阳极转化膜、铬酸盐转化膜、铬酸盐-磷酸盐转化膜、钛或锆盐转化膜、非铬氧化膜、磷化膜等。阳极氧化膜的优点是耐磨和可用于装饰防护，但阳极氧化存在投资大、成本高和耗能高的缺点。虽然铬酸盐氧化的工艺很成熟和完善，而且成本低廉，是比较理想的氧化工艺。但因为铬酸盐氧化后的废液中含有六价铬，处理较费时，严重污染环境，因此开发和研制高效，
节能、环保型的铝合金钝化液势在必行。 1
钝化机制
自制复合盐钝化剂在金属表面形成致密的