城市埋地钢质燃气管道腐蚀成因分析及防护措施
高琨
（北京首都机场动力能源有限公司，北京100621）
摘要：针对城市埋地钢质燃气管道的腐蚀，分析了化学、电化学、细菌、杂散电流等因素对管道扁蚀的影响。燃气管道腐蚀后具有安全隐惠，严重影响供气安全性。为避免燃气管道腐蚀带来的严重后果，提出防治燃气管道腐蚀的措施，以延缓管道腐蚀，保证燃气供应的安全、平稳。
关键词：燃气管道腐蚀；电化学腐蚀；绝缘层防腐；电保护法
中图分类号：TE832.2文献标志码：B文章编号：1009-3230(2016)12-0038-03
CauseAnalysis andProtectionMeasuresofCorrosion
For Urban Buried Steel Gas Pipeline
GAOKun
(Beijing Capital Airport Power &Energy Co.,Ltd.Beijing 100621, China)
Abstract: Based on the corosion of urban buried steel gas pipeline, the paper analyzes the influence of chemical, electrochemical, bacteria, stray current and other factors on the corrosion of pipeline. After the gas pipeline corrosion, it has a safe hidden danger, which seriously affects the safety of gas supply. In order to avoid the serious consequences caused by the corrosion of gas pipeline, the measures to prevent and control gas pipeline corrosion are put forward, so as to delay the corrosion of pipeline and ensure the safety and stability of gas supply.
Key words: Gas pipeline corrosion; Electrochemical corrosion; Insulation layer preservation; Elec-tricalprotectionmethod
0引言
随着我国城市建设的不断发展，城市燃气事业得以迅速发展，地下管网规模也随之扩大。城市燃气作为一种优质、清洁、高效、便捷的能源，也具有易燃、易爆的特点，对管网的安全运行与使用寿命带来极大的危害，因此城市燃气设备设施运行中，运行时间长久，老化魔蚀的燃气管道存在着安全隐患，需要燃气管理部门对此予以高度重视。文中就城市埋地燃气管道的腐蚀成因与防护进行分析和探讨。
收稿日期：2016-1005
修订日期：2016-1128
作者简介：高瑶（1985-），女，硕士研究生，助理工程师，
从事燃气运行管理及技术研究工作。
万方数据
1燃气钢质管道腐蚀的原因
腐蚀是金属在周围介质的化学、电化学作用下引起的一种破坏。金属腐蚀按其性质可分为化
学腐蚀和电化学腐蚀。 1.1化学腐蚀
化学腐蚀是金属直接和介质接触发生化学作用而引起金属被溶解的过程。由于输送的燃气中可能含有硫化氢、二氧化硫或其它腐蚀性化合物，直接和金属反应，引起化学腐蚀，燃气管道壁厚是均匀地减薄的。化学腐蚀主要发生在管道内壁，防腐根本措施是将燃气净化，使其杂质含量达到允许值以下；还可以在管道内用合成树脂或环氧树脂等作内涂层，防止管道内壁的腐蚀，并能降低