阀控铅酸蓄电池阻燃壳体性能研究
邵双喜
（双登集团股份有限公司，江苏泰州225500）
摘要：本文通过垂直法对阀控铅酸蓄电池阻燃壳休进行燃烧性能实验，制定了阻燃壳体阻燃性能的实验标准。研究了酒精浓度、温度及干燥和酒精擦顺序等对阻燃壳体的耐化学性能的影响，得出了电池壳体不易经高温和高浓度酒精处理，同时电池壳体应具有一定的时效时间，这样电池壳体不易产生裂纹。
关键词：阀控铬酸蓄电池；阻燃壳体；阻燃性能；耐化学性能
文章编号：1006-0847(2013)05-213-04
中图分类号：TM912.1
文献标识码：B
Studyontheperformanceofflameretardantcontainerof
VRLAbattery SHAOShuang-xi
(Shuangdeng Group Co., Lid., Taizhou Jiangsu225500, China)
Abstract: In this article, the author did a combustibility test of the flame retardant container through vertical method, and set the test standard. The influence of concentration and temperature of alcohol, drying along with wiping sequence on the chemical resistance of the flame retardant container was mainly studied. The study came to a conclusion that battery containers made basically no changes after high temperature and high concentration alcohol treatment. And in the meantime the battery container should pass a certain ageing time to avoid crack.
Key words:VRLA battery; flame retardant container;flame retardation; chemical resistance
0引言
ABS树酯是20世纪40年代开发的热塑性工程塑料，由丙烯腈（A）、丁二烯（B）和苯乙烯（S）三元共聚物组成。三者之间具有良好的协同性能：丙烯睛的引入保留了ABS树酯的刚性和耐药品
收稿日期：2013-05-16 万方数据
性，丁二烯的引入提高了ABS树酯的柔韧性和抗冲击性，苯乙烯的引入优化了ABS树酯的光泽和加工流动性。由于这些优点，使得ABS树脂得到广泛的应用。它因具有优异的电性能、化学稳定性和抗冲击性而成为电器元件、家电、计算机和仪器仪表首选的塑料之一"]。然而，ABS树脂的氧指数仅为18.3~20（<21），属于易燃材料[2)，在空气中容易燃烧，且在燃烧过程中释放出大量有毒有害的气体，如HCN、CO等，并产生黑烟，这一缺点无疑严重地制约着ABS树脂的应用发展。因此，ABS的阻燃问题越来越受到世界各国的高度重