AGM隔膜纤维不同排列方向对 VRLA电池电解液分层的影响
沈维海，朱潇
（中材科技膜材料公司，江苏南京210012）
摘要：通过零距抗张强度来表征AGM隔膜中玻璃纤维纵横向排列的比例，以研完纤维纵横向的分布对铅酸蓄电池电解液分层的影响。试验结果表明，AGM隔膜纤维纵横向排列差异越小，越有利于改善电解液分层，从而提高铬酸蓄电池循环寿命
关键词：AGM隔膜；纤维分布；毛细吸酸速率；零距抗张强度；电解液分层；铅酸蓄电池
中图分类号：TM912.1
文献标识码：B
文章编号：1006-0847(2015)05-227-03
Theeffectoffiberatthree-directionarrayinAGMseparatoron
theelectrolyte stratificationofVRLAbattery
SHENWei-hai,ZHUXiao
(Sinomatech Membrane Material Company,Nanjing Jiangsu 210012,China
Abstract: The ratio of glass fiber at M/D and C/D distribution in AGM separator is characterized by the zero span tensile strength. The effect of glass fiber at M/D and C/D distribution array on the electrolyte stratification in lead-acid battery is studied in this paper. Experimental result shows that the smaller difference of M/D and C/D distribution array is more beneficial to reduce the electrolyte stratification and to enhance the cycle life of lead-acid batteries.
Key words: AGM separator; M/D and C/D distribution; capillary acid absorption rate, zero span tensile strength; electrolyte stratification; lead-acid battery
1概述
阀控式铅酸蓄电池（VRLA电池）是目前使用最为广泛的一类二次电池，应用于汽车、摩托车、电动自行车等起动或动力电源，以及计算机和通信设备的备用电源，未来清洁能源如风能、太阳能、
收稿日期：201503-03
潮汐能等的储能电源。近年来铅酸蓄电池的工艺有了很大的改进，其性能也有了较大的提高，但由于电池本身系统的原因，电解液的分层仍是一个驱待解决的难题。
最初电解液注入铅酸蓄电池时，整个溶液的密
度是均匀的。但在充放电过程中，由于电化学反应的进行，放电时新生成的水会向上浮，而充电时生成的酸由于密度大会向下沉，使得铅蓄电池在使用一段时间之后，其电解液的密度上小下大，最终降低蓄电池的循环寿命"