提高小型阀控式铅酸蓄电池寿命的研究
李洪刚
（卧龙电气集团浙江灯塔电源有限公司，浙江绍兴321000
试验研究
摘要：研究了极群装配压力和加酸量两个设计因素对起动用小型间控式铅酸蓄电池（简称阀控式铅酸蓄电池）循环寿命的影响。实验结果表明：当极群装配压力在35～70kPa且加酸量在 9mL/Ah时循环寿命最好，可超过400次。并且蓄电池初期容量和低温高倍率放电性能也较好。
关键词：间控式铅酸蓄电池；循环寿命：极群装配压力：加酸量中图分类号：TM912.1
文献标识码：B文章编号：1006-0847(2012)03-115-03
StudyontheimprovementofcyclelifeofsmallVRLAbat-
LI Honggang
(Zhejiang Dengta Power Source Co., Lid., Wolong Electric Group, Shaoxing Zhejiang 32IO00, China)
Abstract: The article studied the influence of two design factors, i.e. assemhling pressure of plates and volume of filled electrolyte, on the cycle lives of the starting valveregulated leadacid batteries (hereafter called as VRLA batteries). The experiment results showed that the lives of VRLA batteries could reach 400 cyeles when the assembling pressure of plates reached 35 ~ 70 kPa and the volume of filled electrolyte reached 9 mL/Ah. And the initial capacity and lower temperature discharging performance of VRLA
hatteries are better than those under other conditions.
0前言
1968年德赛（Desai）提交了第一篇描述气体密封铅酸蓄电池的专利，1971年美国盖茨公司研制出商品化的圆筒形密封铅酸蓄电池后，在近40 多年中，随着阀控式铅酸蓄电池生产技术的不断成熟，其质量也在不断地提高。由于它具有不漏液、析气少、免维护、可以任意方向放置等优点而被广泛应用于多个行业。但是每个生产广在设计和生产工艺上各有千秋，致使阀控式铅酸蓄电池的寿命也参差不齐。一般铅酸蓄电池失效的主
收稿日期：2011-11-08
要原因有正极板栅腐蚀变形、活性物质软化脱落、负极板栅汇流排腐蚀、电解液干凋、不可道硫酸盐化等因素"。笔者通过对不同极群装配压力和不同加酸量的实验，提出调整这两个设计参数可以解决上述的一些问题，使阀控式铅酸蓄电池
的循环寿命有很大程度的提高。 1试验过程及条件
本文所试验的电池型号为GTX4L-BS阀控式铅酸蓄电池，此型号电池采用热封结构，每个极群由3片正极板和4片负极板组成。电池壳单格有效尺寸为：98mm×27mm×98mm；极板尺寸为： 72mm×42mm×1.7(1.2)mm；隔板长宽为90mm× 80mm(双层)。因为电池壳单格有效尺寸和极板的