阀控式铅酸蓄电池用粘合剂及密封工艺的研究
谢爽
（沈阳蓄电池研究所，辽宁沈阳110142）
摘要：选用不同的胺类树脂制成复合固化剂，根据阀控式铅酸蓄电池的不同结构和大小制备不同要求的粘合剂，并根据工艺环境及任务量确定密封工艺。这种粘合剂具有良好的耐腐性、耐候性(高温或低温)和粘接强度，并易于操作。
关键词：阀控式铅酸蓄电池；粘合剂；固化剂；环氧树脂；聚氢酯
中图分类号：TM912.9
文献标识码：B
文章编号：1006-0847(2010)06-267-03
StudyontheadhesiveandthesealingprocessforVRLAbatteries
XIEShuang
(ShenyangStorageBatteryResearchInstitute,ShenyangLiaoning10l42)
Abstract:Some different amino resin was chosen to make into composite curing agent. We prepared different adhesives to meet different requirements according to the different structures and sizes of the valveregulated leadacid batteries, The sealing technology was determined on the basis of the technical environment and tasks. This adhesive had better corrosion resistance, weather resistance (high or low temperature) and adhesive strength, and was easy lo operate.
Key words: valveregulated leadacid battery; adhesive; curing agent; epoxy resin; Polyurethane
1概述
阀控式铅酸蓄电池（VRLA蓄电池）的密封方式主要有两种：一种是采用热封的密封方式，另一种是采用粘合剂密封方式。前者槽、盖的主要材料是聚内烯树脂（PP），后者主要是丙烯-苯乙烯共聚物（AS）和丙烯腈-苯乙烯-丁二烯共聚(共混）物（ABS)。对VRLA蓄电池而言，气密和液密是至关重要的，密封性能的好坏直接影响到蓄
收稿日期：2010-10-21 万方数据
电池的性能，特别是寿命。一旦密封性能达不到要求，失水过度，番电池自放电和硫酸盐化将加快，电池的容量会出现快速衰减，导致寿命提前终止。
在常见的密封不良的VRLA蓄电池中，主要表现在电解液会沿蓄电池槽与盖密封不良处外漏，单格间串气，或产生极柱“爬酸”现象，或兼而有之。其结果是蓄电池寿命提前终止。此外还会因酸液（酸雾）外溢污染环境，腐蚀设备和电池架体及连接电缆，影响系统的正常运行，严重时还会因漏液导致电池起火、燃烧。
在已知的VRLA詩电池各类故障中，密封不良占有较大的比例。由粘合剂密封引起的密封不良主要是粘合剂性能和密封工艺欠佳，与槽、盖变形