超声微波辅助制备铅炭材料及
其在铅酸电池中的应用
卢东亮”，周攀，赵瑞瑞”，陈红雨
实验研究
www.batterychn.com
（1.广产东环境保护工程职业学院循环经济与低碳经济系，广产东佛山528216：
2.华南师范大学化学与环境学院，广东广州510006）
摘要：本文中，采用超声微波辅助制备了一种铅炭材料，将该材料作为负极添加剂应用到铬酸蓄电池中，电池表现出了优异的容量和良好的循环性能。并且，针对添加量进行探完的结果表明，当该铅炭材料添加的质量分数为0.2%时，电池的性能最佳
关键词：铅炭材料；负极板；添加剂；铅酸蓄电泡；铅炭电泡；超声微波
中图分类号：TM912.9
文献标识码：A
文章编号：1006-0847(2017)01-01-04
SynthesisofPb-C compositebyultrasonic/microwaveassisted
techniqueandtheusageinlead-carbonbattery
LU Dongliang', ZHOU Pan', ZHAO Ruirui°, CHEN Hongyu
(I. Department of Circular Economy and Low Carbon Economy, Guangdong Polytechnic o) Environmental Protection Engineering, Foshan Guangdong 528216; 2. School of Chemistry and Environment, South China Normal University, Guangzhou Guangdong 5/0006, China)
Abstract: A Pb-C composite was synthesized by an ultrasonic/microwave assisted technique. When this material was used as a negative additive in lead-acid battery, the battery exhibited a superior performance. The research results of lead-acid batteries with different content of Pb-C composite showed that when the content was 0.2 wt.%, the performance of battery was best.
Keywords: lead-carbon material; negative plate; additive; lead-acid battery; lead-carbon battery; ultrasonic/microwave
0引言
铅酸蓄电池在电动汽车以及起/停应用时，大部分情况下处于高倍率部分荷电状态（HRPSoC）下运行。在此运行工况下，传统铅酸蓄电池中的氧
收稿日期：2016-10-31
基金项目：广东省高等职业教育品牌专业建设项目—工业节能技术专业建设项目（2016gzpp035）
万方数据
化产物硫酸铅颗粒不能及时得以还原为铅，导致负极板的硫酸铅颗粒越来越大，从而产生严重的硫酸盐化现象，进而导致电池失效。
在铅酸蓄电池中加入炭材料构建铅炭电池是近
年来铅酸蓄电池的一个重要研究方向。在铅酸蓄电池中加入炭材料，能够提高负极活性物质的比表面积和电导率，添加的炭材料可以构建导电网络，从而提高硫酸铅材料的转化率。在铅炭电池的研究工作中，Nakamura等人研究了在负极活性物质中加入炭黑，炭黑的加入改善了铅酸蓄电池在HRPSoC
2017 No.1 Vo1.5401