不同电解液添加剂对蓄电池循环性能的影响
杨勇，梁晶晶？
（1.深圳瑞达电源有限公司，深圳518000；2.沈阳蓄电池研究所，辽宁沈阳110142）
摘要：验证SnSO,作为电解液添加剂的效采，并与使用纳来SiO,与K,SO,的组合添加剂进行对
比，通过循环测试验证其实际效果并对其差异进行对比和分析。关键词：SnSO4；电解液添加制；纳米SiO,与K,SO4：循环寿命
9文献标识码：B文章编号：1006—0847(2011)04-157-03
中图分类号：TM912.9
Acomparisonofcylelifebyusingdifferentelectrolyteadditives
YANG Yong', LIANG Jingjing
(1. Shenzhen Ritar Power Co., Lid., Shenzhen 518000; 2. Shenyang Storage Battery Research
Institute,ShenyangLiaoning110142)
Abstract: SnSO, was proved as an effective additive used in VRLA batteries. When SnSO, was added into the electrolyte or PAM, it would increase the capacity and the charge acceptance of leadacid batteries, so it would prevent the PCL-1 of VRLA effectively. By using a new additive which was made of SiO and K,SO
was used to replace SnSO, in experimental result shows the same effect as SnSO Key words: SnSO: additive in electrolyte; nano SiO, and K,SO: cycle life
1前言
SnSO.作为添加剂用于阀控式铅蓄电池，已被证明具有良好的效果，主要可以提高薪电池的充电接受能力、防止PCL-1、增加电池循环寿命和提高容量等围。把SnSO.加人电解液中与在活性物中添加具有相似的效果围。采用纳米SiO,与K,SO,组合
使用同样可以达到相似的效果。 2实验
2.1实验准备
收稿日期：2010-12-14 万方数据
按完全相同的装配方式制造3只样品蓄电池，所用的极板、隔板、槽等均相同：正、负极板配组后进行组装，3+4-/单体装配，正极3片均为 140±0.5g；负极4片均为117±0.5g。电解液密度为1.33g/mL；电解液加人量约62mL/单体，具体参数见表1。2"和3*样品在此基础上添加了
定量的添加剂(分析纯级）。 2.2实验内容
幕电池经过相同的初充电化成后，按C（即以1.944A放电至10.5V）进行放电，然后在限压 14.3V（模拟实际充电偏低的情况）的条件下，以电流1.4A充电8h构成一个循环，循环测试至放出容量低于75%（4.5Ah）时终止。同时测试一只YUASA的NP7-12，并进行对比。
0uNo.4Val.4857