不同掺炭比例对超级电池负极铅膏
电化学性能的影响许树茂，陈杰勇，邓淇彬，高爱梅，舒东（华南师范大学化学与环境学院，广东广州510006）
摘要：本文通过三电极体系模拟超级铬酸电池的工作环境，探讨其负极铬膏的电化学性能。并探讨分别以板栅和钛片为集流体对其电化学性能的影响及其含炭量分别在0%～2%和8%～24% 间的最佳含炭比例。
关键词：超级电池；负极铅膏；钛片；最佳含炭量
中图分类号：TM912.9
文献标识码：A
文章编号：1006-0847(2013)05-231-06
Electrochemicalresearchontheinferenceofcarbondopedwith different ratio on the electrochemical performance of negative
lead paste of ultralead-acid battery
XU Shu-mao,CHEN Jie-yong,DENG Qi-bin,GAOAi-mei,SHU Dong*(SchoolofChemistry andEnvironment,SouthChinaNormal University
GuangzhouGuangdong510006,China)
Abstract:By imitating the working conditions of lead-acid battery with three-electrode system,thc electrochemical performance of the negative lead paste of lead-acid battery is researched on different collectors: titanium foil and lead grid. The optimal mass ratio of carbon to the negative paste is also studied within the range of 0 % ~ 2 % and 8 % ~ 24 %.
Key words: ultra-battery; negative lead paste; titanium foil; optimal carbon content
0前言
铅酸电池具有价格低、大电流放电性能良好，电池回收率高等优点。然而，铅酸电池由于质量比能量低（35~40Wh/kg）、使用寿命短（300~800
收稿日期：2013-01-23*通讯联系人
万方数据
次）、快速充电困难等缺点限制了其应用。近些年涌现了许多铅酸电池新技术，其中超级电池是最受关注的技术之一。它将超级电容器与铅酸电池并联到一个单体中，将电容器的高比功率、长寿命的优势融合到铅酸电池中，提高功率同时，延长了电池使用寿命[-2]。
本文通过三电极体系模拟超级铅酸电池的工作环境，探讨其负极铅膏的电化学性能。并探讨分别以板棚栅和钛片为集流体对其电化学性能的影响及其含炭质量分数分别在0%~2%和8%~24%间的最佳含炭比例。