镀锡、铋对铅钙锡合金阳极膜性能的影响
苏丽青，盘华玉"，郭永榔1，赵文超”，刘孝伟？，周龙瑞？
（1.福州大学化学化工学院，福建福州350108；2.超威电源有限公司，浙江长兴313100）
摘要：通过电化学况积法在Pb-Ca-Sn合金表面镀锡、钛，采用叠加交流伏安法、线性电势扫描法、交流阻抗法等研究了其合金电极在疏酸溶液中生长的阳极膜性质。结果表明，经电镀表面处理的电极不但能够有效地抑制阳极膜中导电性差的Pb(IⅡI)化合物的形成，促进PbOu(0 关键词：电化学阻抗；阳极膜；铅钙锡合金；镀锡和链
中图分类号：TM912.4
文献标识码：A
文章编号：1006-0847(2011)01-16-04
Influence of tinning and bismuth plating on anodic
corrosionfilmsonPb-Ca-Snelectrodes
SU Liqing', PAN Huayu', GUO Yonglang, ZHAO Wenchao, LIU Xiaowei?, ZHOU longrui2(l. College of Chemistry and Chemical engineering, Fuzhou University, Fuzhou Fujian 350108
2. Chaowei Power Co.,Ltd, Changxing Zhejiang313100, China)
Abstract: Tin and bismuth metals were plated on PbCaSn alloy. The properties of the anodic films formed on PbCaSn alloy with and without tinning and bismuth plating were studied by ac voltammetry, linear sweep voltammetry and electrochemical impedance spectroscopy (EIS). The results show that the plated alloy electrodes inhibit the growth of the Pb(ll) compounds with poor conductivity in the anodic film, promote the growth of PbO (O Key words: anodic flm; electrochemical impedance spectroscopy; PbCaSn alloy; tinning and bismuth plating
1前言
目前铅酸蓄电池板栅合金主要是采用铅钙锡合金和铅锑合金。铅钙锡合金不但析氢过电势高，可减少气体析出量，降低电池自放电速度，而且耐腐蚀，被广泛用作免维护铅酸薪电池板栅材料-。然而，铅钙合金的表面容易生成导电性差的钝化
收稿日期：2010-11-12 16oiNa.ival4 万方数据
膜-7，影响了电池的充电接受能力和深循环寿命。在铅钙合金中添加锡，能够显著提高钝化膜的导电性，从而抑制板栅钝化8-9。Prengaman/10-/等人在铅钙锡合金中添加铋，发现铋易形成富锡和富铋的区域，有利于提高板栅与活性物质的结合力，提高深放电性能和循环寿命，并且不会增大析氢反应速度。然而金属锡、铭价格昂贵，加人量大会加大成本。为了降低成本并有效防止正极板栅钝化，采用电沉积法在Pb-Ca-Sn正极板栅表面镀上锡、铋金属，并研究其在硫酸溶液中的电化学行为。