核电站超低碳不锈钢薄壁管焊接技术难点研究
李伟龙
（国核工程有限公司，上海200233）
摘要：针对岭澳二期核电站核岛安装工程中超低碳不锈钢薄壁管道对接烊遥到的难点进行了分析和解决，通过采用合理的焊接方法和工艺参数，以及相应的烊接技巧，解决了焊接过程中薄壁管的变形问题和接头容易氧化的问题。
关键词：Z2CN18.10；不锈钢薄壁管；TIG；氢气室、背面送丝工艺中图分类号：TM623.3
文献标志码：B文章编号：1009-3230(2015)03-0035-04
35
Nuclear PowerPlant in theSuper Low Carbon Stainless Steel Pipe
WeldingTechnologyofThin-walledResearchDifficulties
LI Wei long
(StateNuclearPowerEngineering Company,Shanghai200233,China）
Abstract: Aiming at the difficulty of Ling Ao phase two nuclear island installation project in butt welding low carbon stainless steel thin wall pipe encountered are analyzed and solved, by using reasonable welding method and process parameters, and the corresponding welding technique, solves the problem of thin walled tube in the process of welding deformation problem of easy oxidation and jointproblems.
Key words: Z2CN18. 10; Thin wall stainless steel pipe; TIG; Argon chamber; The back wire feeding process
0引言
岭澳二期核电站是法国引进堆型经过国产化研制改进后的两台百万千瓦级大型商用核电站，由于核电站设计寿命较长，安全性要求很高，工艺管道内工况多为高温、高压、腐蚀性强、带有放射性的介质，因此在核岛内部大量采用超低碳不锈钢作为管道材料，其最具代表性的材料为Z2CN18.10。对于不锈钢薄壁管，焊接过程存在着焊接变形、根部氧化和焊缝接头及两侧母材表面过烧等问题。其中变形间题导致现场管道安装困难，局部应力集中，严重影响工程质量。针对以上难点本文进行了研究和试
收稿日期：201502-10 作者简介：李伟龙
万方数据
修订日期：20150221
验，通过采用合适的焊接方法和工艺参数，以及对焊工进行培训提高焊接技能等方法成功解决了上述向题。
1焊接难点及原因分析
奥氏体不锈钢具有热导系数小，热膨胀系数大的特点，见表1，这就决定了在同样的情况下不锈钢的焊接变形比碳钢更为明显（1)。对接焊接头中，随着焊缝熔池不断的凝固，后续焊道受到先前焊道的拘束作用，产生收缩变形，其影响工程安装质量的主要变形形式为横向收缩变形。焊接收缩变形的主要影响因素是焊接线能量，而线能量一般由焊接参数所决定。因而选取合适的焊接电流、电压和焊接速度是控制焊接变形的有效途径之一。
不锈钢在焊接时经过多次热循环作用，若焊